Experimental Confirmation of Ni5Al3 Phase in Ni-Al Binary System by Diffusion Couple Technique

被引：0
|
作者：
Li Changfa [1 ]
Ren Yuping [2 ]
Qin Gaowu [2 ]
机构：
[1] Tianjin Univ Technol, Sch Mat Sci & Engn, Tianjin 300384, Peoples R China
[2] Northeastern Univ, Key Lab Anisotropy & Mat MOE, Shenyang 110004, Peoples R China
来源：
MATERIALS AND MANUFACTURING, PTS 1 AND 2 | 2011年 / 299-300卷
关键词：
Ni-Al binary system; Diffusion couple technique; Ni5Al3; Phase diagram; SHAPE-MEMORY ALLOY; INTERMETALLIC COMPOUNDS;
D O I：
10.4028/www.scientific.net/AMR.299-300.224
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The equilibrium phase relationships and compositions of Ni - 51at.%Al/Ni - 26at.%Al diffusion couple heat treated at 650 degrees C for various times have been investigated by means of diffusion couple technique. Experimental results showed that Ni5Al3 phase was not only stable at 650 degrees C, but also had a large solubility range (45.3 similar to 40.6) at.% Al. The obtained relationships of NiAl/Ni5Al3 and Ni5Al3/Ni3Al are in accordance with the current generally accepted Ni-Al binary system phase diagram, but their composition ranges are quite different from the presently accepted one, that is, the the phase boundaries of NiAl / (Ni5Al3 + NiAl), (Ni5Al3 + NiAl) / Ni5Al3 and Ni5Al3 / (Ni3Al + Ni5Al3) significantly shift to the Al-rich side.
引用
收藏
页码：224 / +
页数：2
相关论文
共 50 条
  • [21] Diffusion mobilities for the B2-b.c.c. phase in the Ni-Al binary system
    Wei, Hua
    Hou, Guichen
    Sun, Xiaofeng
    Guan, Hengrong
    Hu, Zhuangqi
    JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 454 (1-2) : 400 - 405
  • [22] Ni2Al versus Ni5Al3 ordering in Ni65Al35 austenite and martensite
    Schryvers, D
    Toth, L
    VanHumbeeck, J
    Beyer, J
    JOURNAL DE PHYSIQUE IV, 1995, 5 (C8): : 1029 - 1033
  • [23] Microstructure evolution and forming mechanism of Ni-Al solid/liquid diffusion couple
    Jiang, Shu-Ying
    Li, Shi-Chun
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2010, 20 (08): : 1552 - 1557
  • [24] Ni5Al3 phase in heat cycled nickel-rich NiAl
    Cheng, T
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1996, 15 (04) : 285 - 289
  • [25] Directional solidification and phase equilibria in the Ni-Al system
    Hunziker, O
    Kurz, W
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (12): : 3167 - 3175
  • [26] Directional solidification and phase equilibria in the Ni-Al system
    O. Hunziker
    W. Kurz
    Metallurgical and Materials Transactions A, 1999, 30 : 3167 - 3175
  • [27] Directional solidification and phase equilibria in the Ni-Al system
    Rolls-Royce University Technology Centre, Department of Materials Science and Metallurgy, University of Cambridge, Cambridge CB2 3QZ, United Kingdom
    不详
    Metall Mat Trans A Phys Metall Mat Sci, 12 (3167-3175):
  • [28] Phase stability of Ni-Al nanoparticles
    de Debiaggi, SR
    Campillo, JM
    Caro, A
    JOURNAL OF MATERIALS RESEARCH, 1999, 14 (07) : 2849 - 2854
  • [29] THEORETICAL AND EXPERIMENTAL INVESTIGATION OF THE PHASE-DECOMPOSITION PROCESS OF NI-RICH NI-AL SYSTEM
    CHOO, WK
    LEE, JS
    KIM, DG
    PARK, SS
    SCRIPTA METALLURGICA, 1989, 23 (10): : 1779 - 1784
  • [30] EXPERIMENTAL-ANALYSIS OF THE NI-AL PHASE-DIAGRAM
    BREMER, FJ
    BEYSS, M
    KARTHAUS, E
    HELLWIG, A
    SCHOBER, T
    WELTER, JM
    WENZL, H
    JOURNAL OF CRYSTAL GROWTH, 1988, 87 (2-3) : 185 - 192
12345