Tribological properties of a-C : N and a-C films prepared by shielded arc ion plating

被引：13
|
作者：
Tajima, N [1 ]
Saze, H [1 ]
Sugimura, H [1 ]
Takai, O [1 ]
机构：
[1] Nagoya Univ, Grad Sch Engn, Dept Mat Proc Engn, Chikusa Ku, Nagoya, Aichi 4648603, Japan
来源：
VACUUM | 2000年 / 59卷 / 2-3期
关键词：
D O I：
10.1016/S0042-207X(00)00317-1
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Amorphous carbon nitride (a-C:N) and amorphous carbon (a-C) thin films that rarely contained hydrogen were synthesized on Si(100) wafers by means of shielded are ion plating. Nanomechanical properties of these films were studied in relation to substrate bias voltage. The a-C film prepared at a DC bias voltage of 100 V showed a maximal hardness of 35 GPa, whereas the film deposited at - 500 V had a minimal hardness of 7 GPa. Wear resistance was excellent for films with hardness greater than 20 GPa when rubbed with a diamond tip at a contact force of 20 muN. Hardness of the a-C : N films, remained in the range of 10-14 GPa, independent of the bias voltage. However, the wear resistance of the a-C :N films was much better than that of the hard a-C films. In particular, the a-C : N film prepared at - 300 V was so wear resistant that the film did not wear at all. (C) 2000 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：567 / 573
页数：7
相关论文
共 50 条
  • [41] Microstructure and Tribological Properties of Pulsed Laser Deposited WSx/a-C Composite Films
    Yang Fanger
    Lu Ye
    Zhang Ji
    Lin Lingling
    Chang Xinxin
    Zheng Xiaohua
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 : 177 - 181
  • [42] Tribological and mechanical properties of nanocrystalline-TiC/a-C nanocomposite thin films
    Musil, J.
    Novak, P.
    Cerstvy, R.
    Soukup, Z.
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2010, 28 (02): : 244 - 249
  • [43] The preparation and tribological properties of nc-TiC/a-C nanocomposite multilayer films
    Laboratory of Special Functional Materials, Henan University, Kaifeng
    475000, China
    不详
    475000, China
    Mocaxue Xuebao, 2 (190-197):
  • [44] Mechanical properties of a-C:H and a-C:H/SiOx nanocomposite thin films prepared by ion-assisted plasma-enhanced chemical vapor deposition
    Lee, JH
    Kim, DS
    Lee, YH
    Farouk, B
    THIN SOLID FILMS, 1996, 280 (1-2) : 204 - 210
  • [45] Influence of Si on the Microstructure and Mechanical and Tribological Properties of Ag/a-C:H Films
    Wu, Yanxia
    Zhang, Shujiao
    Meng, Jie
    Wang, Shengxi
    Yu, Shengwang
    Ma, Yong
    Tang, Bin
    Liu, Ying
    Komvopoulos, Kyriakos
    TRIBOLOGY TRANSACTIONS, 2020, 63 (05) : 897 - 905
  • [46] Tribological properties of hard a-C:H:F coatings
    Jaoul, C.
    Dublanche-Tixier, C.
    Jarry, O.
    Tristant, P.
    Lavoute, J. P.
    Kilman, L.
    Colas, M.
    Laborde, E.
    Ageorges, H.
    SURFACE & COATINGS TECHNOLOGY, 2013, 237 : 328 - 332
  • [47] Effect of methane on magnetron sputtering graphite target deposited films and tribological properties of a-C:H:Ti/a-C:H friction pairs
    Wen, Xinyu
    Lai, Zhenguo
    Zhang, Bin
    Wang, Xin
    Wang, Yuan Yuan
    Gao, Kaixiong
    Tao, Caihong
    SURFACE AND INTERFACE ANALYSIS, 2022, 54 (09) : 933 - 943
  • [48] Influence of Gamma Irradiation on Microstructure, Mechanical Properties and Tribological Properties of a-C: H Films
    Chai L.
    Ning K.
    Qial L.
    Wang P.
    Weng L.
    Mocaxue Xuebao/Tribology, 2021, 41 (02): : 169 - 175
  • [49] Cathodoluminescence of the a-C:N films deposited by a filtered cathodic arc plasma system
    Hsieh, WJ
    Lin, CC
    Chen, US
    Chang, YS
    Shih, HC
    DIAMOND AND RELATED MATERIALS, 2005, 14 (01) : 93 - 97
  • [50] Tribological properties of a-C:H films on Si substrate prepared by plasma CVD in pulse-biased process
    Wazumi, K
    Koga, Y
    Tanaka, A
    DIAMOND AND RELATED MATERIALS, 2003, 12 (3-7) : 1018 - 1023
12345