Tribological properties of a-C : N and a-C films prepared by shielded arc ion plating

被引：13
|
作者：
Tajima, N [1 ]
Saze, H [1 ]
Sugimura, H [1 ]
Takai, O [1 ]
机构：
[1] Nagoya Univ, Grad Sch Engn, Dept Mat Proc Engn, Chikusa Ku, Nagoya, Aichi 4648603, Japan
来源：
VACUUM | 2000年 / 59卷 / 2-3期
关键词：
D O I：
10.1016/S0042-207X(00)00317-1
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Amorphous carbon nitride (a-C:N) and amorphous carbon (a-C) thin films that rarely contained hydrogen were synthesized on Si(100) wafers by means of shielded are ion plating. Nanomechanical properties of these films were studied in relation to substrate bias voltage. The a-C film prepared at a DC bias voltage of 100 V showed a maximal hardness of 35 GPa, whereas the film deposited at - 500 V had a minimal hardness of 7 GPa. Wear resistance was excellent for films with hardness greater than 20 GPa when rubbed with a diamond tip at a contact force of 20 muN. Hardness of the a-C : N films, remained in the range of 10-14 GPa, independent of the bias voltage. However, the wear resistance of the a-C :N films was much better than that of the hard a-C films. In particular, the a-C : N film prepared at - 300 V was so wear resistant that the film did not wear at all. (C) 2000 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：567 / 573
页数：7
相关论文
共 50 条
  • [31] a-C∶F∶H films prepared by PECVD
    刘雄飞
    肖剑荣
    简献忠
    王金斌
    高金定
    Transactions of Nonferrous Metals Society of China, 2004, (03) : 426 - 429
  • [32] a-C : F : H films prepared by PECVD
    Liu, XF
    Xiao, JR
    Jian, XZ
    Wang, JB
    Gao, JD
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2004, 14 (03) : 426 - 429
  • [33] Tribological properties of a-C:H multilayer structures
    Knoblauch-Meyer, L
    Hauert, R
    THIN SOLID FILMS, 1999, 338 (1-2) : 172 - 176
  • [34] Tribological properties of TiC/a-C:H nanocomposite coatings prepared via HiPIMS
    Sanchez-Lopez, J. C.
    Dominguez-Meister, S.
    Rojas, T. C.
    Colasuonno, M.
    Bazzan, M.
    Patelli, A.
    APPLIED SURFACE SCIENCE, 2018, 440 : 458 - 466
  • [35] Scanning tunneling spectroscopy of a-C:H and a-C:(H, Cu) films prepared by magnetron sputtering
    Zvonareva, TK
    Ivanov-Omskii, VI
    Rozanov, VV
    Sharonova, LV
    SEMICONDUCTORS, 2001, 35 (12) : 1398 - 1403
  • [36] Optical properties of a-C and a-C:H diamond-like films prepared by high power excimer laser ablation
    Chen Bao-Ling
    Zhao Li-Xin
    Zhang Bing
    Chen Yu-Qiang
    Yang Xin-Hui
    Peng Hong-Yan
    Jin Zeng-Sun
    CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2006, 27 (06): : 1012 - 1015
  • [37] Scanning tunneling spectroscopy of a-C:H and a-C:(H, Cu) films prepared by magnetron sputtering
    T. K. Zvonareva
    V. I. Ivanov-Omskii
    V. V. Rozanov
    L. V. Sharonova
    Semiconductors, 2001, 35 : 1398 - 1403
  • [38] Mechanical properties and Raman spectra of a-C:H and a-C:H:N coatings
    Vyskocil, J
    Siroky, P
    Vorlicek, V
    Perina, V
    DIAMOND AND RELATED MATERIALS, 1996, 5 (3-5) : 466 - 470
  • [39] Tribological properties of a-C:H:N thin films prepared using C2H2 and N2 by CFUBM sputtering method
    Park, Yong Seob
    Cho, Hyung Jun
    Hong, Byungyou
    THIN SOLID FILMS, 2008, 516 (19) : 6655 - 6659
  • [40] Electrical conductivity and structural properties of a-C:N films deposited by ion-assisted pulse-arc sputtering
    Streletskiy, O. A.
    Zavidovskiy, I. A.
    Nischak, O. Yu
    Dvoryak, S., V
    THIN SOLID FILMS, 2020, 701
12345