In-situ high temperature X-ray diffraction study on the phase transition process of polymetallic sulfide ore

被引：3
|
作者：
Li, Guangshi [1 ]
Cheng, Hongwei [1 ,2 ]
Xiong, Xiaolu [1 ]
Lu, Xionggang [1 ,2 ]
Xu, Cong [1 ]
Lu, Changyuan [1 ]
Zou, Xingli [1 ,2 ]
Xu, Qian [1 ,2 ]
机构：
[1] Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China
[2] Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China
来源：
2ND INTERNATIONAL CONFERENCE ON MINING, MATERIAL AND METALLURGICAL ENGINEERING | 2017年 / 191卷
关键词：
CHALCOPYRITE; NICKEL; OXIDATION; XRD;
D O I：
10.1088/1757-899X/191/1/012037
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The phase transformation of the polymetallic sulfide ore is quite complicated, especially the variety and diversity of the roasted intermediate. The mineralogy properties of the ore particles were characterized by XRF, ICP and SEM-EDS. The thermal stability of the complex ore was investigated using TG-DSC under different atmosphere (pure N-2 and 1% O-2-N-2). The phase changes and intermediates were revealed by the in-situ XRD in pure N-2 and 1% O-2-N-2 atmospheres with the temperature range from 25 to 800 degrees C. These results indicated that the crystal transformation of the pyrrhotite from monoclinic to hexagonal at 320 degrees C, and the pentlandite and chalcopyrite were decomposed into monosulfide solid solution in pure N-2. While the pentlandite and chalcopyrite were completely oxidized into M*xFe3-xO4 (M*=Fe, Ni, Cu) and Fe2O3, which is also the final product of the ore sample oxidized under 1% O-2-N-2 atmosphere.
引用
收藏
页数：6
相关论文
共 50 条
  • [31] IN-SITU HIGH PRESSURE X-RAY DIFFRACTION STUDY ON CuGeO3.
    Shieh, S. R.
    Mao, H. K.
    Hemley, R. J.
    Jayaraman, A.
    ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 1999, 55 : 556 - 556
  • [32] In-situ X-ray diffraction measurement of electrodeposition process in molten salts
    Kajinami, A
    Deki, S
    Umesaki, N
    Sato, M
    Myochin, M
    NEW FRONTIERS OF PROCESSING AND ENGINEERING IN ADVANCED MATERIALS, 2005, 502 : 335 - 338
  • [33] In-situ characterization of the carbon nanotube growth process by X-ray diffraction
    Baehtz, Carsten
    Wirth, C. Tobias
    Bayer, Bernhard C.
    Hofmann, Stephan
    von Borany, Johannes
    ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 2011, 67 : C123 - C124
  • [34] In-situ X-ray diffraction study of phase transformations in the Am-O system
    Lebreton, Florent
    Belin, Renaud C.
    Delahaye, Thibaud
    Blanchart, Philippe
    JOURNAL OF SOLID STATE CHEMISTRY, 2012, 196 : 217 - 224
  • [35] Design and application of a high-temperature microfurnace for an in situ X-ray diffraction study of phase transformation
    Eu, W. S.
    Cheung, W. H.
    Valix, M.
    JOURNAL OF SYNCHROTRON RADIATION, 2009, 16 : 842 - 848
  • [36] An in situ high-temperature X-Ray diffraction study of phase transformations in maraging 300 steel
    Reis A.G.D.
    Reis D.A.P.
    Abdalla A.J.
    Couto A.A.
    Otubo J.
    1600, Trans Tech Publications Ltd (371): : 73 - 77
  • [37] In situ high-temperature X-Ray diffraction study of tantalum metal
    Si-Ahmed, Fariza
    Afir, Arezki
    Pialoux, Andre
    Chikh, Houria
    MAIN GROUP CHEMISTRY, 2023, 22 (03) : 453 - 467
  • [38] In situ x-ray diffraction study of the antiferroelectric-ferroelectric phase transition in PLSnZT
    Blue, CT
    Hicks, JC
    Park, SE
    Yoshikawa, S
    Cross, LE
    APPLIED PHYSICS LETTERS, 1996, 68 (21) : 2942 - 2944
  • [39] In situ characterization of phase transformations in petroleum pitch by high temperature X-ray diffraction
    Vautard, F.
    Cakmak, E.
    Arnould, M.
    Watkins, T. R.
    Paul, R.
    Meyer III, H.
    Damron, J.
    Gallego, N.
    Lara-Curzio, E.
    FUEL, 2023, 331
  • [40] In-situ observation of CuInSe2 formation process using high-temperature X-ray diffraction analysis
    Katsui, A
    Iwata, T
    THIN SOLID FILMS, 1999, 347 (1-2) : 151 - 154
12345