Arsenic incorporation in HgCdTe grown by molecular beam epitaxy

被引：7
|
作者：
Aqariden, F [1 ]
Wijewarnasuriya, PS [1 ]
Sivananthan, S [1 ]
机构：
[1] Univ Illinois, Dept Phys, Microphys Lab, Chicago, IL 60607 USA
来源：
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B | 1998年 / 16卷 / 03期
关键词：
D O I：
10.1116/1.589844
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
We report the results of in situ doping of HgCdTe by molecular beam epitaxy (MBE) using an elemental arsenic source. Arsenic was successfully incorporated as an acceptor during the MBE growth using either a conventional or planar doping approach. Hall effect measurements and secondary ion mass spectroscopy (SIMS) were used to investigate arsenic activity before and after different Hg anneals. Close to 100% acceptor doping efficiency with arsenic was obtained on these MBE grown layers after annealing. This corresponds to a total arsenic concentration of approximately 2 X 10(18) cm(-3) which is more than sufficient for a wide range of infrared devices. At much higher total arsenic concentration, electrical activity falls off drastically. (C) 1998 American Vacuum Society.
引用
收藏
页码：1309 / 1311
页数：3
相关论文
共 50 条
  • [21] Crystallinity improvement of HgCdTe on GaAs grown by molecular beam epitaxy
    Sasaki, Tokuhito
    Tomono, Mitsuko
    Oda, Naoki
    [J]. Journal of Crystal Growth, 1995, 150 (1 -4 pt 2): : 785 - 789
  • [22] The incorporation behavior of arsenic and antimony in GaAsSb/GaAs grown by solid source molecular beam epitaxy
    Wu, SD
    Guo, LW
    Wang, WX
    Li, ZH
    Shang, XZ
    Hu, HY
    Huang, Q
    Zhou, JM
    [J]. JOURNAL OF CRYSTAL GROWTH, 2004, 270 (3-4) : 359 - 363
  • [23] Arsenic incorporation and its influence on microstructure of wurtzite GaN grown by molecular-beam epitaxy
    [J]. Kim, H.J. (hyonju.kim@fys.kuleuven.ac.be), 1600, American Institute of Physics Inc. (94):
  • [24] Arsenic incorporation and its influence on microstructure of wurtzite GaN grown by molecular-beam epitaxy
    Kim, HJ
    Andersson, TG
    Chauveau, JM
    Trampert, A
    [J]. JOURNAL OF APPLIED PHYSICS, 2003, 94 (11) : 7193 - 7200
  • [25] Incorporation of Mg in GaN grown by molecular beam epitaxy
    Univ of Nottingham, Nottingham, United Kingdom
    [J]. J Cryst Growth, 1-2 (7-11):
  • [26] IN INCORPORATION IN GAINAS GROWN BY MOLECULAR-BEAM EPITAXY
    WOODBRIDGE, K
    [J]. APPLIED PHYSICS LETTERS, 1992, 60 (23) : 2911 - 2913
  • [27] Incorporation of Mg in GaN grown by molecular beam epitaxy
    Orton, JW
    Foxon, CT
    Cheng, TS
    Hooper, SE
    Novikov, SV
    Ber, BY
    Kudriavtsev, YA
    [J]. JOURNAL OF CRYSTAL GROWTH, 1999, 197 (1-2) : 7 - 11
  • [28] Mode of arsenic incorporation in HgCdTe grown by MBE
    Sivananthan, S
    Wijewarnasuriya, PS
    Aqariden, F
    Vydyanath, HR
    Zandian, M
    Edwall, DD
    Arias, JM
    [J]. JOURNAL OF ELECTRONIC MATERIALS, 1997, 26 (06) : 621 - 624
  • [29] Mode of arsenic incorporation in HgCdTe grown by MBE
    S. Sivananthan
    P. S. Wijewarnasuriya
    F. Aqariden
    H. R. Vydyanath
    M. Zandian
    D. D. Edwall
    J. M. Arias
    [J]. Journal of Electronic Materials, 1997, 26 : 621 - 624
  • [30] CRYSTALLINITY IMPROVEMENT OF HGCDTE ON GAAS GROWN BY MOLECULAR-BEAM EPITAXY
    SASAKI, T
    TOMONO, M
    ODA, N
    [J]. JOURNAL OF CRYSTAL GROWTH, 1995, 150 (1-4) : 785 - 789
12345