The Study on Oxidation Resistance Properties of Ductile Cast Irons for Exhaust Manifold at High Temperatures

被引：10
|
作者：
Yang, Yun-long [1 ]
Cao, Zhan-yi [1 ]
Qi, Yang [1 ]
Liu, Yong-Bing [1 ]
机构：
[1] Jilin Univ, Key Lab Automobile Mat, Minist Educ, Changchun 130025, Peoples R China
来源：
MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5 | 2010年 / 97-101卷
关键词：
oxidation behavior; high Si-Mo ductile cast iron; exhaust manifold; ductile Ni-resist cast iron; CORROSION;
D O I：
10.4028/www.scientific.net/AMR.97-101.530
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The oxidation behavior of two ductile cast irons was investigated in this paper. The alloys were a high Si-Mo ductile and a ductile Ni-Resist cast iron which were developed by FAW Foundry. Polished sections were exposed at temperatures between 800 degrees C and 1000 degrees C, mostly for 80h. It has been found that the property of oxidation resistance of ductile Ni-Resist cast iron is excellent or better than that of high Si-Mo ductile by comparison and analysis.
引用
收藏
页码：530 / 533
页数：4
相关论文
共 50 条
  • [31] Relationships between microstructure and mechanical properties in ductile cast irons:: a review
    Castillo, R
    Bermont, V
    Martínez, V
    REVISTA DE METALURGIA, 1999, 35 (05) : 329 - 334
  • [32] Graphite Nodularity Evaluation in High-Si Ductile Cast Irons
    Riposan, Iulian
    Anca, Denisa
    Stan, Iuliana
    Chisamera, Mihai
    Stan, Stelian
    MATERIALS, 2022, 15 (21)
  • [33] MECHANICAL PROPERTIES AND WEAR RESISTANCE OF WHITE CAST IRONS
    PARENTSI.S
    MARGERIE, JC
    FONDERIE, 1973, 28 (319): : 15 - 27
  • [34] MECHANICAL PROPERTIES AND WEAR RESISTANCE OF WHITE CAST IRONS
    PARENTSIMONIN, S
    MARGERIE, JC
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1972, 69 (12): : 809 - 823
  • [35] Wear resistance of high chromium -: high carbon cast irons
    Maldonado-Ruíz, SI
    Velasco, A
    Colás, R
    López, D
    INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2003, 15 (06) : 589 - 594
  • [36] A study on the oxidation characteristics of cast irons containing aluminum
    Ghosh, S
    Prodhan, A
    Mohanty, ON
    Chakrabarti, AK
    OXIDATION OF METALS, 1996, 45 (1-2): : 109 - 131
  • [37] Influence of austempering temperatures on microstructure and wear performance of solution strengthened ferritic ductile cast irons
    Teker, T.
    Yilmaz, S. O.
    Bulus, E.
    PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2024, 61 (06): : 356 - 369
  • [38] Evaluation of fatigue properties on shot-peening treated ductile cast irons
    Ochi, Y
    Sekino, T
    Matsumura, T
    Masaki, K
    PROCEEDINGS OF THE SEM IX INTERNATIONAL CONGRESS ON EXPERIMENTAL MECHANICS, 2000, : 42 - 45
  • [39] Microstructure and Mechanical Properties of As-Cast Ductile Irons Alloyed with Manganese and Copper
    Ranjan Kumar Dasgupta
    Dipak Kumar Mondal
    Ajit Kumar Chakrabarti
    Ashis Chandra Ganguli
    Journal of Materials Engineering and Performance, 2012, 21 : 1728 - 1736
  • [40] Microstructure and Mechanical Properties of As-Cast Ductile Irons Alloyed with Manganese and Copper
    Dasgupta, Ranjan Kumar
    Mondal, Dipak Kumar
    Chakrabarti, Ajit Kumar
    Ganguli, Ashis Chandra
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2012, 21 (08) : 1728 - 1736
12345