The flexural strength at high temperature and oxidation behaviour of (Nb,Ti)C-Ni composite

被引：6
|
作者：
Cai, KF
Nan, CW
Yuan, RZ
Min, XM
机构：
[1] Natl. Lab. Adv. Technol. Mat. C., Wuhan University of Technology, Wuhan
来源：
CERAMICS INTERNATIONAL | 1996年 / 22卷 / 02期
关键词：
D O I：
10.1016/0272-8842(95)00075-5
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
(Nb,Ti)C-Ni composite is prepared via hot isostatic pressing (HIP). Its flexural strength at elevated temperature is tested by means of three-point bending. The flexural strength, as a function of temperature, decreases at 700 degrees C, and more rapidly decreases with further increase in temperature. At 1000 degrees C, the flexural strength (about 325 MPa) is only 20% of that at room temperature. The oxidation behaviour of the composite in the temperature range from 850 degrees C to 1100 degrees C. is also studied. The composite is oxidized into TiO2, NiO and NiTiO3 at high temperature. The oxidation kinetics are parabolic, with an activation energy of 234 kJ/mol.
引用
收藏
页码：167 / 170
页数：4
相关论文
共 50 条
  • [41] High temperature strength, fracture toughness and oxidation resistance of Nb-Si-Al-Ti multiphase alloys
    Murayama, Yonosuke
    Hanada, Shuji
    SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2002, 3 (02) : 145 - 156
  • [42] Oxidation behavior of Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2C-Mx C (M = Ti, Zr, Hf, Nb, Ta) composite ceramic at high temperature
    Xu, Shuai
    Wang, Tao
    Wang, Xingang
    Wu, Lu
    Fang, Zhongqiang
    Ge, Fangfang
    Meng, Xuan
    Liao, Qing
    Wei, Jinchun
    Li, Bingsheng
    CHINESE PHYSICS B, 2023, 32 (06)
  • [43] Oxidation behaviors of Ti44Ni47Nb9 shape memory alloy at high temperature
    Tao, BW
    Liu, JH
    Li, SM
    ACTA METALLURGICA SINICA, 2005, 41 (06) : 633 - 637
  • [44] The influence of high energy milling and sintering parameters on reactive sintered (Ti, Mo) C-Ni cermets
    Joeleht, Marek
    Pirso, Jueri
    Juhani, Kristjan
    Viljus, Mart
    Traksmaa, Rainer
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 636 : 381 - 386
  • [45] HIGH TEMPERATURE OXIDATION BEHAVIOUR OF TiAl8Nb ALLOY
    Przybylski, K.
    Prazuch, J.
    Brylewski, T.
    Durda, E.
    ARCHIVES OF METALLURGY AND MATERIALS, 2013, 58 (02) : 477 - 480
  • [46] Effect of alloying elements on oxidation behavior of Nb-Ti-Al-C alloys at high temperature
    Wei, Wen-Qing
    Jiang, Jun-Sheng
    Lu, Shu-Tian
    Cui, Da-Wei
    Wei, Zun-Jie
    Zhang, Peng
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2015, 36 (05): : 54 - 60
  • [47] Effect of milling on the carbothermal reduction of oxide mixture for (Ti,W)C-Ni
    Kwon, Hanjung
    Kang, Shinhoo
    MATERIALS TRANSACTIONS, 2008, 49 (07) : 1594 - 1599
  • [48] Oxidation behavior of Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2C-MxC(M=Ti,Zr,Hf,Nb,Ta) composite ceramic at high temperature
    徐帅
    王韬
    王新刚
    吴璐
    方忠强
    葛芳芳
    蒙萱
    廖庆
    魏金春
    李炳生
    Chinese Physics B, 2023, (06) : 726 - 734
  • [49] High-temperature flexural strength and reliability of Ti(C5N5)-TiB2-(W7Ti3) C composite cermet tool material
    Liu, Yue
    Huang, Chuanzhen
    Zou, Bin
    Liu, Hanlian
    Liu, Guoliang
    CERAMICS INTERNATIONAL, 2017, 43 (15) : 12511 - 12518
  • [50] Tuning microstructure for superb mechanical properties in a Ti(C, N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature
    Zhao, Xianrui
    Du, Xunbai
    Li, Zhanjiang
    Zuo, Dunwen
    Zhao, Yangyang
    Zhang, Qiangyong
    Lu, Wenzhuang
    Xu, Feng
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2024, 124
12345