The flexural strength at high temperature and oxidation behaviour of (Nb,Ti)C-Ni composite

被引：6
|
作者：
Cai, KF
Nan, CW
Yuan, RZ
Min, XM
机构：
[1] Natl. Lab. Adv. Technol. Mat. C., Wuhan University of Technology, Wuhan
来源：
CERAMICS INTERNATIONAL | 1996年 / 22卷 / 02期
关键词：
D O I：
10.1016/0272-8842(95)00075-5
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
(Nb,Ti)C-Ni composite is prepared via hot isostatic pressing (HIP). Its flexural strength at elevated temperature is tested by means of three-point bending. The flexural strength, as a function of temperature, decreases at 700 degrees C, and more rapidly decreases with further increase in temperature. At 1000 degrees C, the flexural strength (about 325 MPa) is only 20% of that at room temperature. The oxidation behaviour of the composite in the temperature range from 850 degrees C to 1100 degrees C. is also studied. The composite is oxidized into TiO2, NiO and NiTiO3 at high temperature. The oxidation kinetics are parabolic, with an activation energy of 234 kJ/mol.
引用
收藏
页码：167 / 170
页数：4
相关论文
共 50 条
  • [31] High temperature oxidation and wear behaviour of powder metallurgically developed Ni-Cr-W-Al-Ti-MoS2 composite
    Xue, Maoquan
    INDIAN JOURNAL OF ENGINEERING AND MATERIALS SCIENCES, 2009, 16 (02) : 111 - 115
  • [32] High temperature oxidation of Nb-Ti-Al alloys
    ENSCT-INPT, Toulouse, France
    Materials Science Forum, 1997, 251-254 (part 1) : 119 - 126
  • [33] High temperature oxidation of Nb-Ti-Al alloys
    Roos, C
    Oquab, D
    Pieraggi, B
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 4, PTS 1 AND 2, 1997, 251-2 : 119 - 126
  • [34] High temperature oxidation behaviour of Ti2AlC ceramic at 1200°C
    Song, G. M.
    Schnabel, V.
    Kwakernaak, C.
    Van der Zwaag, S.
    Schneider, J. M.
    Sloof, W. G.
    MATERIALS AT HIGH TEMPERATURES, 2012, 29 (03) : 205 - 209
  • [35] Early high temperature oxidation behaviour of Ti(C,N)-based cermets in air
    Yang, Qingqing
    Xiong, Weihao
    Li, Shiqi
    Yao, Zhenhua
    Chen, Xiao
    CORROSION SCIENCE, 2010, 52 (10) : 3205 - 3211
  • [36] High Temperature Flexural, Tensile Strength and Oxidation Behavior of Ti3SiC2 Ceramic at 900°C-1300°C in Ambient Air
    He, R.
    Zhou, Z.
    Qu, Z.
    Cheng, X.
    JOURNAL OF TESTING AND EVALUATION, 2017, 45 (04) : 1150 - 1158
  • [37] Effect of Ball Milling on Microstructure and Flexural Strength of Ti(C,N)-Ni Cermets
    Wang, Xiaoyan
    Li, Jian
    Wu, Ruifen
    Pan, Wei
    HIGH-PERFORMANCE CERAMICS VI, 2010, 434-435 : 76 - 78
  • [38] FERROMAGNETISM IN SEMICONDUCTOR C-Ni FILMS AT DIFFERENT ANNEALING TEMPERATURE
    Dalouji, Vali
    Elahi, Smohammad
    SURFACE REVIEW AND LETTERS, 2016, 23 (03)
  • [39] Raman studies of C-Ni/Ti films deposited on Si (100)
    Belka, R.
    Keczkowska, J.
    Suchanska, M.
    Firek, P.
    Wronka, H.
    Radomska, J.
    Czerwosz, E.
    PHOTONICS APPLICATIONS IN ASTRONOMY, COMMUNICATIONS, INDUSTRY, AND HIGH-ENERGY PHYSICS EXPERIMENTS 2015, 2015, 9662
  • [40] High temperature oxidation behaviour of porous Ni-Si intermetallics at 600 °C and 800 °C
    Wu, Liang
    Liu, Da
    Li, Li
    Wang, Hui
    Mo, Xinya
    Zhang, Haihong
    Zhang, Qiankun
    Xiao, Yifeng
    Kang, Jiangang
    He, Yuehui
    Yang, Guangyao
    JOURNAL OF ALLOYS AND COMPOUNDS, 2025, 1010
12345