Corrosion resistance of GdPO4 thermal barrier coating candidate in the presence of CMAS+NaVO3 and CMAS

被引：23
|
作者：
Guo, Lei [1 ,2 ]
Feng, Jiayi [1 ]
Meng, Shijun [1 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Tianjin 300072, Peoples R China
[2] Minist Educ, Tianjin Key Lab Adv Joining Technol, Key Lab Adv Ceram & Machining Technol, Tianjin 300072, Peoples R China
来源：
CORROSION SCIENCE | 2022年 / 208卷
关键词：
Thermal barrier coatings; CMAS; CMAS + NaVO 3; Interface reaction layer; Crystalline products; PHASE-EQUILIBRIA; LNPO(4) LN; REPO4; RE; BEHAVIOR; MECHANISM; GD; ND; LA; CONDUCTIVITY; DELAMINATION;
D O I：
10.1016/j.corsci.2022.110628
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
GdPO4 is a promising thermal barrier coating (TBC) candidate owing to its excellent resistance to calciummagnesium-alumina-silicate (CMAS) and molten salt corrosion. In this study, the corrosion behavior of GdPO4 in CMAS + molten salt (CN) was investigated and compared with that in CMAS. At 1200 and 1250 degrees C, interface reaction layers rapidly formed on both the CN and CMAS attacked GdPO4 pellets, and many crystalline products were generated in the melts. This effectively increased the melt viscosity and suppressed its penetration. As compared to CMAS, CN was more aggressive to GdPO4 at 1200 degrees C but less at 1250 degrees C.
引用
收藏
页数：10
相关论文
共 50 条
  • [31] CMAS corrosion and thermal cycle of Al-modified PS-PVD environmental barrier coating
    Zhang, Xiaofeng
    Zhou, Kesong
    Liu, Min
    Deng, Changguang
    Deng, Chunming
    Niu, Shaopeng
    Xu, Shiming
    Su, Yifan
    CERAMICS INTERNATIONAL, 2018, 44 (13) : 15959 - 15964
  • [32] Hot corrosion of high-entropy hafnate for thermal barrier coating material subjected to molten CMAS
    Cong, Longkang
    Li, Wei
    Song, Qiang
    Guo, Yao
    Wang, Jiancheng
    Gu, Shengyue
    Zhang, Shouyang
    CORROSION SCIENCE, 2022, 209
  • [33] Corrosion behavior of CMAS coupling NaVO3 salt for plasma-sprayed Al2O3/YSZ thermal barrier coatings
    Zhang, Yongang
    Han, Jiasen
    Wu, Dongting
    Zou, Yong
    CORROSION SCIENCE, 2023, 221
  • [34] Corrosion Resistance of Al2O3 Coating Prepared by Filtered Cathodic Vacuum Arc for Thermal Barrier Coatings Against CMAS Degradation
    Tao, Liu
    Qing, He
    Dan, Li
    RARE METAL MATERIALS AND ENGINEERING, 2022, 51 (11) : 3981 - 3988
  • [35] Corrosion Resistance of Al2O3 Coating Prepared by Filtered Cathodic Vacuum Arc for Thermal Barrier Coatings Against CMAS Degradation
    Liu, Tao
    He, Qing
    Li, Dan
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2022, 51 (11): : 3981 - 3988
  • [36] Rare Earth Silicate Environmental Barrier Coating Material: High-Entropy Design and Resistance to CMAS Corrosion
    Wang Jingyang
    Sun Luchao
    Luo Yixiu
    Tian Zhilin
    Ren Xiaomin
    Zhang Jie
    ACTA METALLURGICA SINICA, 2023, 59 (04) : 523 - 536
  • [37] Grain boundary infiltration and corrosion mechanism of CMAS attack on M-YTaO 4 thermal barrier coating ceramics at 1300 ° C
    Chen, Zhilin
    Tian, Zhilin
    Zheng, Liya
    Li, Bin
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2024, 44 (12) : 7277 - 7284
  • [38] Comprehensive investigation on CMAS and steam corrosion resistance of quaternary rare earth oxide co-doped zirconia thermal barrier coating material
    Shen, Hongyu
    Zhang, Guangheng
    Zhang, Jie
    Wang, Lu
    Wang, Jingyang
    CORROSION SCIENCE, 2025, 244
  • [39] Laser surface modification to improve the resistance of CMAS plus molten salt coupling corrosion to thermal barrier coatings
    Wu, Jing
    Gao, Yuan
    Guo, Cean
    Guo, Lei
    CERAMICS INTERNATIONAL, 2023, 49 (19) : 32282 - 32291
  • [40] Plasma sprayed Yb4Hf3O12 thermal barrier coatings with excellent thermophysical properties and robust CMAS corrosion resistance
    Dang, Xian
    Yuan, Jieyan
    Wang, Jinshuang
    Li, Xinyang
    Huang, Zhulin
    Hu, Xiaoye
    Li, Yue
    CERAMICS INTERNATIONAL, 2023, 49 (16) : 27473 - 27485
12345