Corrosion resistance of GdPO4 thermal barrier coating candidate in the presence of CMAS+NaVO3 and CMAS

被引：23
|
作者：
Guo, Lei [1 ,2 ]
Feng, Jiayi [1 ]
Meng, Shijun [1 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Tianjin 300072, Peoples R China
[2] Minist Educ, Tianjin Key Lab Adv Joining Technol, Key Lab Adv Ceram & Machining Technol, Tianjin 300072, Peoples R China
来源：
CORROSION SCIENCE | 2022年 / 208卷
关键词：
Thermal barrier coatings; CMAS; CMAS + NaVO 3; Interface reaction layer; Crystalline products; PHASE-EQUILIBRIA; LNPO(4) LN; REPO4; RE; BEHAVIOR; MECHANISM; GD; ND; LA; CONDUCTIVITY; DELAMINATION;
D O I：
10.1016/j.corsci.2022.110628
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
GdPO4 is a promising thermal barrier coating (TBC) candidate owing to its excellent resistance to calciummagnesium-alumina-silicate (CMAS) and molten salt corrosion. In this study, the corrosion behavior of GdPO4 in CMAS + molten salt (CN) was investigated and compared with that in CMAS. At 1200 and 1250 degrees C, interface reaction layers rapidly formed on both the CN and CMAS attacked GdPO4 pellets, and many crystalline products were generated in the melts. This effectively increased the melt viscosity and suppressed its penetration. As compared to CMAS, CN was more aggressive to GdPO4 at 1200 degrees C but less at 1250 degrees C.
引用
收藏
页数：10
相关论文
共 50 条
  • [21] Enhanced CMAS and hot corrosion degradation of YSZ thermal barrier coating with nano powders
    Ozcelik, Abdulkadir
    Eker, Aysegul Akdogan
    Karabas, Muhammet
    Avci, Ali
    Kucukyildirim, Bedri Onur
    SURFACE & COATINGS TECHNOLOGY, 2024, 481
  • [22] The mechanical and thermal properties, CMAS corrosion resistance, and the wettability of novel thermal barrier material GdTaO4
    Yang, Wenqi
    Ye, Fuxing
    CERAMICS INTERNATIONAL, 2021, 47 (20) : 28685 - 28697
  • [23] Corrosion behaviors and failure mechanism of plasma sprayed Yb2Si2O7/Si environmental barrier coatings exposed to CMAS+NaVO3
    Hu, Xunxun
    Chen, Yongguo
    Guo, Hongbo
    Xu, Huibin
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2025, 45 (03)
  • [24] Investigation of the CMAS thermal corrosion resistance of novel Al2O3/YTaO4 thermal barrier coatings
    Xue, Ting
    Wu, Dongting
    Gao, Wei
    Dou, Mengfan
    Cao, Yingwen
    Zhang, Yongang
    Zou, Yong
    SURFACE & COATINGS TECHNOLOGY, 2024, 494
  • [25] Effect of CMAS Composition on Hot Corrosion Behavior of Gadolinium Zirconate Thermal Barrier Coating Materials
    Deng, Wenzhuo
    Fergus, Jeffrey W.
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2017, 164 (09) : C526 - C531
  • [26] Characterization of stress in a thermal barrier coating during CMAS corrosion using Ce3+ photoluminescence spectroscopy
    Wang, Shuo
    Zhang, Shijie
    Wang, Zong
    Qu, Chuanyong
    Qiu, Wei
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2023, 106 (10) : 6014 - 6025
  • [27] CMAS corrosion resistance, thermal shock resistance and numerical simulation of novel surface micromesh thermal barrier coatings
    Liang, Xiangyu
    Wang, Yi
    Wang, Shanfei
    Liu, Zhuangzhuang
    Suo, Hongli
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2023, 43 (05) : 2164 - 2174
  • [28] Preparation of plasma sprayed nanostructured GdPO4 thermal barrier coating and its hot corrosion behavior in molten salts
    Li, Mingzhu
    Cheng, Yuxian
    Guo, Lei
    Zhang, Chenglong
    Zhang, Yuchen
    He, Sixian
    Ye, Fuxing
    CERAMICS INTERNATIONAL, 2017, 43 (10) : 7797 - 7803
  • [29] Effect of interface roughness on the CMAS plus molten salt (Na2SO4+NaCl+NaVO3) corrosion resistance of EB-PVD thermal barrier coatings
    Hu, Xiaopeng
    Liu, Sai
    Liu, Qing
    Su, Yang
    Wu, Junyao
    Xie, Zhihang
    Guo, Jinwei
    Zhu, Wang
    SURFACE & COATINGS TECHNOLOGY, 2025, 503
  • [30] CMAS corrosion resistance of YSZ thermal barrier coatings enhanced by Pt-Al films
    Wang, Jinshuang
    Lu, Xianjun
    Shu, Chaoxi
    Duan, Zhixing
    Dong, Shujuan
    Lu, Guoqiang
    Zhang, Yixing
    Yuan, Fuhe
    Cao, Xueqiang
    CERAMICS INTERNATIONAL, 2024, 50 (03) : 5111 - 5120
12345