Effects of tetrahedral amorphous carbon film deposited on dental cobalt-chromium alloys on bacterial adhesion

The dental cobalt-chromium alloys are an important biomaterial used in making artificial dentures. Bacterial adhesion to cobalt-chromium alloys usually results in severe complications such as periodontal infection, secondary caries, and denture stomatitis, which have severe adverse impacts on human health. Therefore, an effective method is needed to reduce the bacterial adhesion to dental cobalt-chromium alloys. The aim of this study was to investigate the effects of ta-C films deposited on a dental cobalt-chromium alloy on the adhesion of Streptococcus mutans (ATCC175), Actinomyces viscosus (ATCC19246) and Candida albicans (ATCC76615). A filtered cathodic vacuum arc (FCVA) technique was used to coat the cobalt-chromium alloy with a ta-C film. Atomic force microscopy (AFM), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) were used to analyze the surface characteristics of the coating. Surface roughness was detected. Surface free energy and its components were calculated by measuring the contact angle. The results showed that the maximum sp(3) fraction was achieved at 200 V substrate bias voltage. Compared with uncoated specimens, the ta-C film coated specimens had a lower surface roughness, a higher surface energy and a higher hydrophilicity. Most importantly, the adhesion of the three tested bacterial strains to the ta-C film coated cobalt-chromium alloy was significantly decreased. These results showed that ta-C film surface treatment could significantly reduce the bacterial adhesion to dental cobalt-chromium alloys, suggesting the potential of ta-C film surface treatment in artificial denture applications. (C) 2012 Elsevier B.V. All rights reserved.