Preparation of vanadium powders by calcium vapor reduction of V2O3 under vacuum

被引：12
|
作者：
Wang, Fengkang [1 ,2 ,3 ]
Xu, Baoqiang [1 ,2 ,3 ,4 ]
Wan, Heli [2 ,3 ,4 ]
Yang, Jia [1 ,2 ,3 ,4 ]
Yang, Bin [1 ,2 ,3 ,4 ]
Jiang, Wenlong [1 ,2 ,3 ,4 ]
机构：
[1] State Key Lab Complex Nonferrous Met Resources Cl, Kunming 650093, Yunnan, Peoples R China
[2] Natl Engn Lab Vacuum Met, Kunming 650093, Yunnan, Peoples R China
[3] Yunnan Prov Key Lab Nonferrous Vacuum Met, Kunming 650093, Yunnan, Peoples R China
[4] Kunming Univ Sci & Technol, Fac Met & Energy Engn, Kunming 650093, Yunnan, Peoples R China
来源：
VACUUM | 2020年 / 173卷 / 173期
基金：
美国国家科学基金会;
关键词：
V2O3; Calciothermic reduction; Vanadium powders; HYDROGEN DESORPTION; METALLIC VANADIUM; TITANIUM;
D O I：
10.1016/j.vacuum.2019.109133
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A novel process for synthesizing vanadium powders via calcium vapor reduction of V2O3 under 10 Pa was investigated. The mixture of vanadium trioxide powders and calcium chloride as a flux was the feed preform, and was then reduced by calcium vapor. After reduction, the reduction samples was subjected to a leaching process, the vanadium powders was synthesized by drying and dehydrogenating of the leaching products. The XRD and SEM results of the dehydrogenation products indicated that vanadium were produced and the V particles transformed into clear antler-shaped particles. Vanadium powders (98 wt% V) with 25 ppm H, 1300 ppm N, 1500 ppm O was finally obtained after a dehydrogenation process by Oxygen-nitrogen combined tester (ONH-2000).
引用
收藏
页数：9
相关论文
共 50 条
  • [41] Anharmonicity in the V2O3 Molecule and Thermodynamic Properties of V2O3 in the Gas Phase
    Gusarov, A. V.
    Osina, E. L.
    HIGH TEMPERATURE, 2012, 50 (01) : 56 - 60
  • [42] Preparation of V2O3 by a short process of ammonium salt reduction and its electrocatalytic properties investigation
    Song, Kun
    Wang, Rucheng
    Su, Hang
    Liu, Miao
    Hu, Liwen
    Liu, Caihong
    Liu, Weizao
    Lv, Xuewei
    Xin, Yuntao
    JOURNAL OF ENVIRONMENTAL CHEMICAL ENGINEERING, 2024, 12 (03):
  • [43] Influence of the vacuum interface on the charge distribution in V2O3 thin films
    Schwingenschloegl, U.
    Fresard, R.
    Eyert, V.
    NEW JOURNAL OF PHYSICS, 2009, 11
  • [44] ASSIMILATION AND CHARACTERIZATION OF MONOCRYSTALS OF V2O3 BY VAPOR-PHASE TRANSPORT
    POUCHARD, M
    LAUNAY, JC
    MATERIALS RESEARCH BULLETIN, 1973, 8 (01) : 95 - 104
  • [45] Synthesis and characterization of V2O3 nanocrystals by plasma hydrogen reduction
    Kong, F. Y.
    Li, M.
    Li, D. B.
    Xu, Y.
    Zhang, Y. X.
    Li, G. H.
    JOURNAL OF CRYSTAL GROWTH, 2012, 346 (01) : 22 - 26
  • [46] Preparation and characterization V2O3 nanopowder by solid phase reaction
    Zhang, KF
    Guo, JS
    Tao, CH
    Liu, X
    Li, HL
    Su, ZX
    CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2005, 21 (07) : 1090 - 1092
  • [47] Structure of vanadium oxide (V2O3) grown on Cu3Au(100)
    Niehus, H
    Blum, RP
    Ahlbehrendt, D
    SURFACE REVIEW AND LETTERS, 2003, 10 (2-3) : 353 - 359
  • [48] Formation of V2O3 nanocrystals by thermal reduction of V2O5 thin films
    Ramana, CV
    Utsunomiya, S
    Ewing, RC
    Becker, U
    SOLID STATE COMMUNICATIONS, 2006, 137 (12) : 645 - 649
  • [49] An interpretation of two X-ray studies of vanadium sesquioxide (V2O3)
    Lovesey, SW
    Sivia, DS
    Knight, KS
    PHYSICA B-CONDENSED MATTER, 2002, 318 (04) : 261 - 266
  • [50] ANGULAR-CORRELATION STUDY OF HYPERFINE INTERACTIONS IN VANADIUM SESQUIOXIDE V2O3
    FORKER, M
    SAITOVITCH, H
    SILVA, PRD
    JOURNAL OF PHYSICS C-SOLID STATE PHYSICS, 1984, 17 (06): : 1055 - 1070
12345