Preparation of vanadium powders by calcium vapor reduction of V2O3 under vacuum

被引：12
|
作者：
Wang, Fengkang [1 ,2 ,3 ]
Xu, Baoqiang [1 ,2 ,3 ,4 ]
Wan, Heli [2 ,3 ,4 ]
Yang, Jia [1 ,2 ,3 ,4 ]
Yang, Bin [1 ,2 ,3 ,4 ]
Jiang, Wenlong [1 ,2 ,3 ,4 ]
机构：
[1] State Key Lab Complex Nonferrous Met Resources Cl, Kunming 650093, Yunnan, Peoples R China
[2] Natl Engn Lab Vacuum Met, Kunming 650093, Yunnan, Peoples R China
[3] Yunnan Prov Key Lab Nonferrous Vacuum Met, Kunming 650093, Yunnan, Peoples R China
[4] Kunming Univ Sci & Technol, Fac Met & Energy Engn, Kunming 650093, Yunnan, Peoples R China
来源：
VACUUM | 2020年 / 173卷 / 173期
基金：
美国国家科学基金会;
关键词：
V2O3; Calciothermic reduction; Vanadium powders; HYDROGEN DESORPTION; METALLIC VANADIUM; TITANIUM;
D O I：
10.1016/j.vacuum.2019.109133
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A novel process for synthesizing vanadium powders via calcium vapor reduction of V2O3 under 10 Pa was investigated. The mixture of vanadium trioxide powders and calcium chloride as a flux was the feed preform, and was then reduced by calcium vapor. After reduction, the reduction samples was subjected to a leaching process, the vanadium powders was synthesized by drying and dehydrogenating of the leaching products. The XRD and SEM results of the dehydrogenation products indicated that vanadium were produced and the V particles transformed into clear antler-shaped particles. Vanadium powders (98 wt% V) with 25 ppm H, 1300 ppm N, 1500 ppm O was finally obtained after a dehydrogenation process by Oxygen-nitrogen combined tester (ONH-2000).
引用
收藏
页数：9
相关论文
共 50 条
  • [21] Preparation and characterization of V2O3 powder and film
    Piao, J
    Takahashi, S
    Kohiki, S
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1998, 37 (12A): : 6519 - 6523
  • [22] Preparation and characterization of spherical V2O3 nanopowder
    Zheng, CM
    Zhang, XM
    He, S
    Fu, Q
    Lei, DM
    JOURNAL OF SOLID STATE CHEMISTRY, 2003, 170 (02) : 221 - 226
  • [23] Preparation and characterization of V2O3 powder and film
    Piao, Jinshun
    Takahashi, Seiji
    Kohiki, Shigemi
    Japanese Journal of Applied Physics, Part 1: Regular Papers & Short Notes & Review Papers, 1998, 37 (12 A): : 6519 - 6523
  • [24] A facile pathway to prepare VO2 and V2O3 powders via a carbothermal reduction process
    Wu, Yue-Dong
    Zhang, Guo-Hua
    Wang, Yu
    Xu, Rui
    Chou, Kuo-Chih
    JOURNAL OF SOLID STATE CHEMISTRY, 2018, 265 : 299 - 305
  • [25] Preparation of Titanium Powders from TiO2 by Calcium Vapor Reduction
    Jingang Jia
    Baoqiang Xu
    Bin Yang
    Dongsheng Wang
    Dachun Liu
    JOM, 2013, 65 : 630 - 635
  • [26] Preparation of Titanium Powders from TiO2 by Calcium Vapor Reduction
    Jia, Jingang
    Xu, Baoqiang
    Yang, Bin
    Wang, Dongsheng
    Liu, Dachun
    JOM, 2013, 65 (05) : 630 - 635
  • [27] CHARACTERISTIC ENERGY-LOSS SPECTRA OF VANADIUM AND OF V2O3
    SZALKOWSKI, FJ
    BERTRAND, PA
    SOMORJAI, GA
    PHYSICAL REVIEW B, 1974, 9 (08) : 3369 - 3376
  • [28] Mechanical activation conditions of the Fe2O3 and V2O3 mixture powders in order to obtain a nanometric vanadium spinel ferrite
    Nivoix, V
    Bernard, F
    Gaffet, E
    Perriat, P
    Gillot, B
    POWDER TECHNOLOGY, 1999, 105 (1-3) : 155 - 161
  • [29] The formative temperature of vanadium oxide V2O3, V2O4 and V2O0
    Siemonsen, H
    Ulich, H
    ZEITSCHRIFT FUR ELEKTROCHEMIE UND ANGEWANDTE PHYSIKALISCHE CHEMIE, 1940, 46 : 141 - 145
  • [30] TEMPERATURE DEPENDENCE OF VANADIUM NMR FREQUENCY SHIFT IN V2O3
    JONES, ED
    JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN, 1969, 27 (06) : 1692 - &
12345