Effect of contact pressure and cyclic stress amplitude on fretting fatigue of 45-carbon steel

被引：0
|
作者：
Sun, Weiming [1 ]
Chen, Shuisheng [1 ]
Tu, Liqun [1 ]
机构：
[1] Zhejiang Univ Technol, Coll Mech & Elect Engn, Hangzhou 310032, Peoples R China
来源：
PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4 | 2007年 / 353-358卷
关键词：
fretting fatigue; stress field and strain field; contact pressure; fatigue life;
D O I：
10.4028/www.scientific.net/KEM.353-358.134
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of contact pressure on fretting fatigue in quenched and tempered 45-carbon steel is studied. With an increase in contact pressure, fretting fatigue life is decreased quickly at low contact pressures; however it almost unchanged at high contact pressures. With an increase in cyclic stress amplitude, fretting fatigue life decreased. In the test, concavity is formed at the fretted area accompanying wear. The main crack is initiated at the outer edge corner of the concavity at high contact pressures, and initiated at the middle portion of the fretted area at low contact pressures.
引用
收藏
页码：134 / 137
页数：4
相关论文
共 50 条
  • [41] Effect of mean stress in very high cycle fretting fatigue of a bearing steel
    Teng, Zhenjie
    Wu, Haoran
    Huang, Zhiyong
    Starke, Peter
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 149
  • [42] Fretting fatigue strength properties of pearlitic and bainitic steels with medium carbon steel contact material
    Ochi, Yasuo
    Tateno, Bungo
    Kuroki, Toshiya
    Zairyo/Journal of the Society of Materials Science, Japan, 1998, 47 (10): : 1065 - 1070
  • [43] Effect of maximum applied cyclic stress on fretting fatigue stress distribution of flat-on-flat modified 9Cr-1Mo steel contact: Finite element analysis
    Shiva, V.
    Christopher, J.
    Veerababu, J.
    Parthasarathi, N. L.
    Kannan, R.
    Nagesha, A.
    Vasudevan, M.
    NUCLEAR ENGINEERING AND DESIGN, 2024, 417
  • [44] Effects of cyclic frequency and contact pressure on fretting fatigue under two-level block loading
    Iyer, K
    Mall, S
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2000, 23 (04) : 335 - 346
  • [45] The roles of contact conformity, temperature and displacement amplitude on the lubricated fretting wear of a steel-on-steel contact
    Warmuth, A. R.
    Sun, W.
    Shipway, P. H.
    Royal Society Open Science, 2016, 3 (10):
  • [46] CRACK-PROPAGATION BEHAVIOR IN FRETTING FATIGUE OF S45C CARBON-STEEL
    SATO, K
    FUJII, H
    KODAMA, S
    BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1986, 29 (256): : 3253 - 3258
  • [47] An investigation into the effect of elevated temperatures on fretting fatigue response under cyclic normal contact loading
    Abbasi, F.
    Majzoobi, G. H.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2018, 93 : 144 - 154
  • [48] Effect of contact pressure on torsional fretting fatigue damage evolution of a 7075 aluminum alloy
    Peng, Jinfang
    Wang, Botong
    Jin, Xiao
    Xu, Zhibiao
    Liu, Jianhua
    Cai, Zhenbing
    Luo, Zhiping
    Zhu, Minhao
    TRIBOLOGY INTERNATIONAL, 2019, 137 : 1 - 10
  • [49] Effect of contact pressure on fretting fatigue failure of oil-well pipe material
    Takazaki, Daisuke
    Kubota, Masanobu
    Komoda, Ryosuke
    Oku, Yosuke
    Makino, Taizo
    Sugino, Masaaki
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 101 : 67 - 74
  • [50] Effect of Stress Amplitude on Fretting Fatigue Damage Behavior of Al-Zn-Mg Alloy
    Jiang Xiaosong
    He Guoqiu
    Liu Bing
    Liu Xiaoshan
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 : 136 - 140
12345