Effect of contact pressure and cyclic stress amplitude on fretting fatigue of 45-carbon steel

被引：0
|
作者：
Sun, Weiming [1 ]
Chen, Shuisheng [1 ]
Tu, Liqun [1 ]
机构：
[1] Zhejiang Univ Technol, Coll Mech & Elect Engn, Hangzhou 310032, Peoples R China
来源：
PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4 | 2007年 / 353-358卷
关键词：
fretting fatigue; stress field and strain field; contact pressure; fatigue life;
D O I：
10.4028/www.scientific.net/KEM.353-358.134
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of contact pressure on fretting fatigue in quenched and tempered 45-carbon steel is studied. With an increase in contact pressure, fretting fatigue life is decreased quickly at low contact pressures; however it almost unchanged at high contact pressures. With an increase in cyclic stress amplitude, fretting fatigue life decreased. In the test, concavity is formed at the fretted area accompanying wear. The main crack is initiated at the outer edge corner of the concavity at high contact pressures, and initiated at the middle portion of the fretted area at low contact pressures.
引用
收藏
页码：134 / 137
页数：4
相关论文
共 50 条
  • [21] An experimental study of low cycle fatigue and cyclic stress ratcheting failure of 45 carbon steel
    Yang, XJ
    ACTA METALLURGICA SINICA, 2004, 40 (08) : 851 - 857
  • [22] EFFECT OF RELATIVE SLIP AMPLITUDE ON FRETTING FATIGUE OF HIGH-STRENGTH STEEL
    NAKAZAWA, K
    SUMITA, M
    MARUYAMA, N
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1994, 17 (07) : 751 - 759
  • [23] Effect of contact pressure on fretting fatigue behavior of Ti-1023
    Wu, G. Q.
    Liu, X. L.
    Li, H. H.
    Sha, W.
    Huang, L. J.
    WEAR, 2015, 326 : 20 - 27
  • [24] Contact-evolution based prediction of fretting fatigue life: Effect of slip amplitude
    Madge, J. J.
    Leen, S. B.
    McColl, I. R.
    Shipway, P. H.
    WEAR, 2007, 262 (9-10) : 1159 - 1170
  • [25] Low cycle fatigue and cyclic stress ratcheting failure behavior of carbon steel 45 under uniaxial cyclic loading
    Yang, XJ
    INTERNATIONAL JOURNAL OF FATIGUE, 2005, 27 (09) : 1124 - 1132
  • [26] Influence of Stress Ratio and Contact Pressure on Fretting Fatigue Behavior of Modified 9Cr-1Mo Steel
    Shiva, V.
    Goyal, Sunil
    Parthasarathi, N. L.
    Das, C. R.
    Kannan, R.
    Nagesha, A.
    Borah, Utpal
    Albert, S. K.
    Bhaduri, A. K.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (04) : 2822 - 2831
  • [27] Influence of Stress Ratio and Contact Pressure on Fretting Fatigue Behavior of Modified 9Cr-1Mo Steel
    V. Shiva
    Sunil Goyal
    N. L. Parthasarathi
    C. R. Das
    R. Kannan
    A. Nagesha
    Utpal Borah
    S. K. Albert
    A. K. Bhaduri
    Journal of Materials Engineering and Performance, 2021, 30 : 2822 - 2831
  • [28] Effect of contact stress on fretting fatigue behaviour of 35CrMoA steel under multiaxial nonproportional paths
    Zhou, Zhiqiang
    Liu, Xiaoshan
    He, Guoqiu
    Ge, Bin
    Le, Peiwen
    Li, Jingquan
    Pan, Jiaqi
    Yang, Yang
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2021, 44 (01) : 212 - 224
  • [29] Relationship between local stress amplitude at contact edges and fretting fatigue strength of austenitic stainless steel JIS SUS316
    Omori, Toshihiro
    Morita, Tatsuro
    Okada, Kohei
    Maeda, Hideaki
    TRIBOLOGY INTERNATIONAL, 2015, 92 : 328 - 334
  • [30] Effect of contact pad rigidity on fretting fatigue behavior of NiCrMoV turbine steel
    Jayaprakash, M.
    Mutoh, Yoshiharu
    Asai, Kunio
    Ichikawa, Kunihiro
    Sukarai, Shigeo
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (11) : 1788 - 1794
12345