Effect of electropolishing on corrosion of nuclear grade 316L stainless steel in deaerated high temperature water

被引：73
|
作者：
Han, Yaolei [1 ]
Mei, Jinna [2 ]
Peng, Qunjia [1 ]
Han, En-Hou [1 ]
Ke, Wei [1 ]
机构：
[1] Chinese Acad Sci, Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Peoples R China
[2] Suzhou Nucl Power Res Inst, Suzhou 215004, Peoples R China
来源：
CORROSION SCIENCE | 2016年 / 112卷
基金：
中国国家自然科学基金;
关键词：
Stainless steel; XPS; TEM; High temperature corrosion; NICKEL-BASE ALLOYS; OXIDE-FILMS; SURFACE PREPARATION; DISSOLVED HYDROGEN; PASSIVE FILMS; BEHAVIOR; OXIDATION; CRACKING; GROWTH; 304-STAINLESS-STEEL;
D O I：
10.1016/j.corsci.2016.09.002
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Effect of change in surface composition and microstructure by electropolishing on corrosion of nuclear grade 316L stainless steel in deaerated high temperature water was investigated. The investigation was conducted by comparing the corrosion of electropolished surface (EPS) with that of the 40 nm-colloidal silica slurry polished surface (CPS), which has few composition change as well as few surface residual strain. The result revealed that the EPS had a higher corrosion rate than the CPS, which is attributed to formation of an amount of hydroxide at the EPS. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：625 / 634
页数：10
相关论文
共 50 条
  • [21] Effect of chloride ion on stress corrosion crack growth rate of 316L stainless steel in high temperature pure water
    Lu, Hui
    Du, Dong-Hai
    Chen, Kai
    Zhang, Le-Fu
    Yuanzineng Kexue Jishu/Atomic Energy Science and Technology, 2015, 49 (10): : 1849 - 1854
  • [22] Specific Corrosion Behavior of 316L Stainless Steel in Mineral Water
    Capelle, J.
    Dmytrakh, I.
    Schwab, F.
    Pluvinage, G.
    MATERIALS SCIENCE, 2019, 54 (05) : 728 - 738
  • [23] Specific Corrosion Behavior of 316L Stainless Steel in Mineral Water
    J. Capelle
    I. Dmytrakh
    F. Schwab
    G. Pluvinage
    Materials Science, 2019, 54 : 728 - 738
  • [24] Corrosion behavior of 316L stainless steel in supercritical water environment
    Yoon, JH
    Son, KS
    Kim, HS
    Mitton, B
    Latanision, R
    Yoo, YR
    Kim, YS
    PRICM 5: THE FIFTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-5, 2005, 475-479 : 4207 - 4210
  • [25] Stress corrosion cracking of cold worked 316L stainless steel in high temperature and high pressure pure water
    Du, Dong-Hai
    Shen, Zhao
    Chen, Kai
    Yu, Lun
    Zhang, Le-Fu
    Shi, Xiu-Qiang
    Xu, Xue-Lian
    Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2015, 37 (02): : 196 - 203
  • [26] Effect of Grain Refinement on the Corrosion Resistance of 316L Stainless Steel
    Ura-Binczyk, Ewa
    MATERIALS, 2021, 14 (24)
  • [27] Effect of silane coating on corrosion resistance of 316l stainless steel
    Lin, Yuan-Hua
    Ma, Yu-Cong
    Talha, Mohd
    Li, Bing
    Shi, Yun-Sheng
    Sun, Zhi-Peng
    Tang, Liang
    Surface Technology, 2019, 48 (02): : 220 - 225
  • [28] Effect of TIG welding on corrosion behavior of 316L stainless steel
    Dadfar, M.
    Fathi, M. H.
    Karimzadeh, F.
    Dadfar, M. R.
    Saatchi, A.
    MATERIALS LETTERS, 2007, 61 (11-12) : 2343 - 2346
  • [29] Corrosion of Type 316 stainless steel in deaerated seawater
    不详
    MATERIALS PERFORMANCE, 2012, 51 (10) : 63 - 63
  • [30] Effects of chloride and oxygen on stress corrosion cracking of cold worked 316/316L austenitic stainless steel in high temperature water
    Du, Donghai
    Chen, Kai
    Lu, Hui
    Zhang, Lefu
    Shi, Xiuqiang
    Xu, Xuelian
    Andresen, Peter L.
    CORROSION SCIENCE, 2016, 110 : 134 - 142
12345