Effect of chloride ion on stress corrosion crack growth rate of 316L stainless steel in high temperature pure water

被引：0
|
作者：
Lu, Hui [1 ]
Du, Dong-Hai [1 ]
Chen, Kai [1 ]
Zhang, Le-Fu [1 ]
机构：
[1] School of Nuclear Science and Engineering, Shanghai Jiao Tong University, Shanghai,200240, China
来源：
Yuanzineng Kexue Jishu/Atomic Energy Science and Technology | 2015年 / 49卷 / 10期
关键词：
Compilation and indexing terms; Copyright 2024 Elsevier Inc;
D O I：
10.7538/yzk.2015.49.10.1849
中图分类号：
学科分类号：
摘要：
Drops - Steel corrosion - Growth rate - Austenitic stainless steel - Dissolved oxygen - High temperature corrosion - Chlorine compounds - Cracks - Ions - Nuclear fuels - Residual stresses - Nuclear power plants
引用
收藏
页码：1849 / 1854
相关论文
共 50 条
  • [1] Stress corrosion cracking of cold worked 316L stainless steel in high temperature and high pressure pure water
    Du, Dong-Hai
    Shen, Zhao
    Chen, Kai
    Yu, Lun
    Zhang, Le-Fu
    Shi, Xiu-Qiang
    Xu, Xue-Lian
    Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2015, 37 (02): : 196 - 203
  • [2] Corrosion fatigue crack growth of laser additively-manufactured 316L stainless steel in high temperature water
    Lou, Xiaoyuan
    Othon, Michelle A.
    Rebak, Raul B.
    CORROSION SCIENCE, 2017, 127 : 120 - 130
  • [3] Effects of chloride and oxygen on stress corrosion cracking of cold worked 316/316L austenitic stainless steel in high temperature water
    Du, Donghai
    Chen, Kai
    Lu, Hui
    Zhang, Lefu
    Shi, Xiuqiang
    Xu, Xuelian
    Andresen, Peter L.
    CORROSION SCIENCE, 2016, 110 : 134 - 142
  • [4] Understanding the effect of nitrogen in austenitic stainless steel on the intergranular stress corrosion crack growth rate in high temperature pure water
    Roychowdhury, S.
    Kain, V.
    Neogy, S.
    Srivastava, D.
    Dey, G. K.
    Prasad, R. C.
    ACTA MATERIALIA, 2012, 60 (02) : 610 - 621
  • [5] Corrosion of 316L stainless steel in high temperature water and steam: Mechanisms of corrosion
    Hanbury, Rigel D.
    Was, Gary S.
    JOURNAL OF NUCLEAR MATERIALS, 2024, 599
  • [6] The effect of low temperature heat treatment on stress corrosion crack initiation in machined 316L stainless steel in high-temperature hydrogenated water
    Chang, Litao
    Mukahiwa, Kudzanai
    Duff, Jonathan
    Burke, M. Grace
    Scenini, Fabio
    SCRIPTA MATERIALIA, 2021, 195
  • [7] Effect of pH on corrosion behavior of 316L stainless steel in hydrogenated high temperature water
    Wang, Jiazhen
    Wang, Jianqiu
    Ming, Hongliang
    Zhang, Zhiming
    Han, En-Hou
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2018, 69 (05): : 580 - 589
  • [8] Effects of loading mode and temperature on stress corrosion crack growth rates of a cold-worked type 316L stainless steel in oxygenated pure water
    Lu, Z.
    Shoji, T.
    Takeda, Y.
    Kai, A.
    Ito, Y.
    CORROSION, 2007, 63 (11) : 1021 - 1032
  • [9] On the stress corrosion crack growth behaviour in high temperature water of 316L stainless steel made by laser powder bed fusion additive manufacturing
    Lou, Xiaoyuan
    Song, Miao
    Emigh, Paul W.
    Othon, Michelle A.
    Andresen, Peter L.
    CORROSION SCIENCE, 2017, 128 : 140 - 153
  • [10] Effect of Zinc on Stress Corrosion Crack Growth Rate of Type 316 Stainless Steel
    Du, Donghai
    Chen, Kai
    Zhang, Lefu
    Shi, Xiuqiang
    Yin, Kaiju
    Hedongli Gongcheng/Nuclear Power Engineering, 2017, 38 (02): : 78 - 83
12345