Influence of rapid solidification of Cu-P intermediate alloy on wear resistance of Al-Si alloy

被引：4
|
作者：
Dong Tianshun [1 ]
Cui Chunxiang [1 ]
Liu Shuangjin [1 ]
Yang Lijun [2 ]
Sun Jibing [1 ]
机构：
[1] Hebei Univ Technol, Sch Mat Sci & Engn, Tianjin 300130, Peoples R China
[2] Tianjin Univ, Tianjin 300072, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2008年 / 37卷 / 04期
关键词：
melt-spin; rapid solidification; wear resistance; modification;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this paper, the influence of rapid solidification of Cu-P intermediate alloy on the wear resistance of Al-Si alloy is studied. TEM analysis indicates that under the cooling speed of 10(5)similar to 10(6) degrees C/S, the microstructure of melt-spin Cu-P ribbon consists of nano-grains and a little amount of amorphous areas, and the grain size of Cu3P in Cu-P intermediate alloy is decreased from 5 similar to 40 mu m to 30 similar to 50 nm. After modified by melt-spin intermediate alloy, the wear resistance of Al-Si alloy are better than that of Al-Si alloy modified by massive ones, wear rate is decreased from 0.86% to 0.39%. Therefore, melt-spin treatment of Cu-P intermediate alloy is effective to improve the wear resistance of Al-Si alloy.
引用
收藏
页码：686 / 689
页数：4
相关论文
共 50 条
  • [41] Effect of silicon content on wear resistance and corrosion behaviour of Al-Si eutectic alloy
    Korkut, M. H.
    Eren, H.
    TRIBOLOGY-MATERIALS SURFACES & INTERFACES, 2007, 1 (03) : 154 - 160
  • [42] Effect of SiC particles on crystal growth of Al-Si alloy during laser rapid solidification
    Zhang, K
    Chen, GN
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 292 (02): : 229 - 231
  • [43] Refinement of Primary Si Phase in Hypereutectic Al-Si Alloy by Electrically Assisted Solidification with P Addition
    Jin, Su-Ji
    Shin, Jungho
    Bang, Jong-Won
    Kim, Yoon-Jun
    Jung, Hyun-Do
    Kim, Moon-Jo
    ADVANCED ENGINEERING MATERIALS, 2024, 26 (21)
  • [44] MICROSTRUCTURE AND WEAR OF CAST (AL-SI ALLOY) GRAPHITE COMPOSITES
    DAS, S
    PRASAD, SV
    RAMACHANDRAN, TR
    WEAR, 1989, 133 (01) : 173 - 187
  • [45] Wear behavior of Al-Si alloy impregnated graphite composite
    Goto, H
    Omori, S
    Uchijo, K
    TRIBOLOGY TRANSACTIONS, 2001, 44 (04) : 551 - 558
  • [46] The effect of Ca and P interaction on the Al-Si eutectic in a hypoeutectic Al-Si alloy
    Ludwig, T. H.
    Daehlen, E. Schonhovd
    Schaffer, P. L.
    Arnberg, L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 586 : 180 - 190
  • [47] Research on Wear Resistance of Mg2Si Reinforced Hypereutectic Al-Si Alloy Composite
    Liu, Zheng
    Liu, Xiao-mei
    HYDRAULIC EQUIPMENT AND SUPPORT SYSTEMS FOR MINING, 2013, 619 : 553 - 556
  • [48] Solidification Behavior of Intensively Sheared Hypoeutectic Al-Si Alloy Liquid
    Kotadia, H. R.
    Babu, N. Hari
    Zhang, H.
    Arumuganathar, S.
    Fan, Z.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (04): : 1117 - 1126
  • [49] Solidification and Microstructure of Al-Si Piston Alloy by Melt Ultrasonic Treatment
    Guo Y.
    Dong X.
    Li J.
    Xia F.
    Yang W.
    Bai Y.
    2018, Editorial Office of Chinese Journal of Rare Metals (42): : 713 - 721
  • [50] An Application for Infrared Camera in Analyzing of the Solidification Process of Al-Si Alloy
    Wladysiak, R.
    Kozun, A.
    ARCHIVES OF FOUNDRY ENGINEERING, 2015, 15 (03) : 81 - 84
12345