Influence of rapid solidification of Cu-P intermediate alloy on wear resistance of Al-Si alloy

被引：4
|
作者：
Dong Tianshun [1 ]
Cui Chunxiang [1 ]
Liu Shuangjin [1 ]
Yang Lijun [2 ]
Sun Jibing [1 ]
机构：
[1] Hebei Univ Technol, Sch Mat Sci & Engn, Tianjin 300130, Peoples R China
[2] Tianjin Univ, Tianjin 300072, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2008年 / 37卷 / 04期
关键词：
melt-spin; rapid solidification; wear resistance; modification;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this paper, the influence of rapid solidification of Cu-P intermediate alloy on the wear resistance of Al-Si alloy is studied. TEM analysis indicates that under the cooling speed of 10(5)similar to 10(6) degrees C/S, the microstructure of melt-spin Cu-P ribbon consists of nano-grains and a little amount of amorphous areas, and the grain size of Cu3P in Cu-P intermediate alloy is decreased from 5 similar to 40 mu m to 30 similar to 50 nm. After modified by melt-spin intermediate alloy, the wear resistance of Al-Si alloy are better than that of Al-Si alloy modified by massive ones, wear rate is decreased from 0.86% to 0.39%. Therefore, melt-spin treatment of Cu-P intermediate alloy is effective to improve the wear resistance of Al-Si alloy.
引用
收藏
页码：686 / 689
页数：4
相关论文
共 50 条
  • [1] Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P
    Zhang Henghua
    Duan Haili
    Shao Guangjie
    Xu Luoping
    RARE METALS, 2008, 27 (01) : 59 - 63
  • [2] RAPID PRESSURE SOLIDIFICATION IN AN AL-SI ALLOY
    WU, HC
    CHIN, BA
    JOURNAL OF MATERIALS SCIENCE, 1991, 26 (04) : 993 - 999
  • [3] Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P
    ZHANG Henghua
    RareMetals, 2008, (01) : 59 - 63
  • [4] Study on Absorption Rate of Phosphorus for Hypereutectic Al-Si Alloy Modified with Cu-P
    Zhong Gu
    Wu Zhibin
    Qiu Chu
    Li Yafang
    Nagaumi, Hiromi
    Aluminium Alloys 2014 - ICAA14, 2014, 794-796 : 112 - 117
  • [5] Influence of melt temperature on Rapid solidification of Al-Y and Al-Si alloy system
    Ranganathan, Sathees
    Fredriksson, Hasse
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2009, 62 (4-5) : 515 - 519
  • [6] Influence of melt temperature on Rapid solidification of Al-Y and Al-Si alloy system
    Sathees Ranganathan
    Hasse Fredriksson
    Transactions of the Indian Institute of Metals, 2009, 62 : 515 - 519
  • [7] Improving the wear resistance of Al-Si alloy by ion implantation
    Itoh, Y
    Azuma, H
    Itoh, A
    Hioki, T
    JOURNAL OF MATERIALS RESEARCH, 1997, 12 (12) : 3246 - 3249
  • [8] Microstructure evolution of hypereutectic Al-Si alloy during rapid solidification
    School of Material Science and Engineering, Shanghai University, Shanghai 200072, China
    不详
    Zhongguo Youse Jinshu Xuebao, 2006, 11 (1924-1930):
  • [9] Fluidity of Al-Si(Cu) alloys as affected by alloy solidification modes
    Pan, EN
    Hu, JF
    TRANSACTIONS OF THE AMERICAN FOUNDRYMEN'S SOCIETY, VOL 106, 1998, 106 : 609 - 617
  • [10] Microstructure and Wear Resistance of Hypereutectic Al-Si Alloy with Combined Eu and P Additions
    Mao F.
    Ou L.
    Qiao Y.
    Zhang P.
    Wang Y.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2021, 45 (04): : 393 - 400
12345