Biaxially aligned high Jc YBCO tapes on YSZ buffer layers deposited by IBAD method

被引：0
|
作者：
Hosaka, M [1 ]
Iijima, Y [1 ]
Sadakata, N [1 ]
Saitoh, T [1 ]
Kohno, O [1 ]
Takeda, K [1 ]
机构：
[1] Fujikura Ltd, Koto Ku, Tokyo 135, Japan
来源：
ADVANCES IN CRYOGENIC ENGINEERING MATERIALS, VOL 44, PTS A AND B | 1998年 / 44卷
关键词：
D O I：
暂无
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
High Jc YBCO thin film tapes were continuously fabricated on flexible Ni-based alloy. Biaxially aligned YBCO films were deposited by PLD on textured YSZ buffer layers formed by using (BAD lion-beam-assisted deposition). For the short sample, Jc value of 1.13x10(6)A/cm(2) (77K, 0T) was obtained and 1.1x10(5)A/cm(2) was maintained at 5T (B perpendicular to c) with measured length of 1cm. For the long sample, Jc value of 2.1x10(5)A/cm(2), and Ic value of 20.8A were obtained (77K, 0T) with measured length of 0.7m. Longitudinal uniformity of the long sample was excellent. Self-field a.c. losses of 0.25m length tapes were measured by a.c. four probe method. The results agreed with Norris' prediction of low a.c. losses for thin strip conductors.
引用
收藏
页码：807 / 813
页数：7
相关论文
共 50 条
  • [41] LASER ABLATED YBCO FILMS ON BUFFER LAYERS OF YSZ AND SRTIO3 DEPOSITED ON SAPPHIRE AND MGO SUBSTRATES
    SCHIEBER, M
    ARIEL, Y
    SCHWARTZ, M
    LEVINSKY, M
    MAHARIZY, SSM
    ZHOU, BL
    HAN, SC
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1991, 4 : S268 - S270
  • [42] Microwave properties of YBCO films deposited on in-plane textured CeO2/YSZ buffer layers
    Kawagishi, K
    Komori, K
    Arisawa, S
    Fukutomi, M
    Togano, K
    PHYSICA C, 2000, 341 : 2405 - 2406
  • [43] Effects of YSZ Buffer Layer Surface Morphology on Superconducting Performance of YBCO films Deposited by Pulsed Laser Deposition on NiW Tapes
    Xiao, G. N.
    Liu, L. F.
    Xu, D.
    Wu, X.
    Luo, Q.
    Li, Y. J.
    11TH EUROPEAN CONFERENCE ON APPLIED SUPERCONDUCTIVITY (EUCAS2013), PTS 1-4, 2014, 507
  • [44] YBCO thick films on alumina substrates with sprayed YSZ buffer layers
    Matsuoka, Y
    Ban, E
    Ogawa, H
    Kurosawa, K
    JOURNAL OF ALLOYS AND COMPOUNDS, 1996, 239 (01) : 55 - 62
  • [45] YBCO coated nickel-based tapes with various buffer layers
    Donet, S
    Weiss, F
    Sénateur, JP
    Chaudouet, P
    Abrutis, A
    Teiserskis, A
    Saltyte, Z
    Selbmann, D
    Eickemeyer, J
    Stadel, O
    Wahl, G
    Jimenez, C
    Miller, U
    JOURNAL DE PHYSIQUE IV, 2001, 11 (PR11): : 319 - 323
  • [46] A comparison of buffer layer architectures on continuously processed YBCO coated conductors based on the IBAD YSZ process
    Holesinger, TG
    Foltyn, SR
    Arendt, PN
    Jia, QX
    Dowden, PC
    DePaula, RF
    Groves, JR
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) : 3359 - 3364
  • [47] Jc anisotropy for magnetic field angle in YBCO coated conductor on IBAD-MgO buffered metal tapes
    Suzuki, H.
    Yoshida, Y.
    Ichino, Y.
    Takai, Y.
    Awaji, S.
    Watanabe, K.
    Yoshizumi, M.
    Izumi, T.
    Shiohara, Y.
    Kato, T.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2010, 470 (20): : 1384 - 1387
  • [48] Biaxially aligned buffer layers of cerium oxide, yttria stabilized zirconia, and their bilayers
    Gnanarajan, S
    Katsaros, A
    Savvides, N
    APPLIED PHYSICS LETTERS, 1997, 70 (21) : 2816 - 2818
  • [49] Microstructure Analysis of High-Quality Buffer Layers on Textured NiW Tapes for YBCO Coated Conductors
    Liu, Linfei
    Zhao, Zuncheng
    Liu, Huaran
    Li, Yijie
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2010, 20 (03) : 1561 - 1564
  • [50] Properties of sprayed YSZ buffer layers on alumina substrates for YBCO thick films
    Matsuoka, Y
    Ban, E
    JOURNAL OF ALLOYS AND COMPOUNDS, 1998, 268 (1-2) : 226 - 232
12345