Influence of Mn-Ni alloying elements on surface film and pitting resistance of Cr-Mn austenitic stainless steels

被引：14
|
作者：
Qu, H. P. [1 ]
Chen, H. T. [1 ]
Lang, Y. P. [1 ]
机构：
[1] CISRI, Inst Special Steels, 76 Haidiannan Rd, Beijing, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2016年 / 125卷
关键词：
Stainless steel; XPS; Argon sputter; Passive film; Pitting potential; PASSIVE FILM; CORROSION BEHAVIOR; HIGH-TEMPERATURE; XPS; CHLORIDE; AES; INCLUSIONS; MANGANESE;
D O I：
10.1016/j.conbuildmat.2016.08.059
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This research focused on surface film and corrosion resistance of three commercial type 200 austenitic stainless steels including L4, L1 and LH with different Mn/Ni mass ratio in Chinese market. X-ray photoelectron spectrum (XPS) results showed that Fe, Cr and Mn oxide layer thickness and passive film thickness were reduced as Mn/Ni mass ratio increased. Mn enrichment was only found in LH passive film. Mn oxide percentage in LH passive film was also the highest. These disadvantages deteriorated pitting resistance of LH, which was proved by anodic polarization result. Mn/Ni mass ratio should not be higher than 1.7 to ensure good corrosion resistance and low raw material cost. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：427 / 437
页数：11
相关论文
共 50 条
  • [41] Carbide transformations in Cr-Ni and Cr-Mn complex alloyed steels
    Vinokur, BB
    MICROSTRUCTURES AND MECHANICAL PROPERTIES OF AGING MATERIALS II, 1996, : 99 - 110
  • [42] Corrosion cracking, structure and properties of hardened Cr-Mn austenitic steels with nitrogen
    Goykhenberg, Yu.N.
    Zhuravlev, L.G.
    Mirzayev, D.A.
    Zhuravleva, V.V.
    Silina, Ye.P.
    Vnukov, V.Yu.
    Physics of Metals and Metallography, 1988, 65 (06): : 83 - 89
  • [43] TIG and MIG welding of high strength Cr-Mn and Cr-Ni alloyed austenitic stainless steel combinations
    Kalacska, E.
    Varbai, B.
    Ginsztler, J.
    Majlinger, K.
    11TH HUNGARIAN CONFERENCE ON MATERIALS SCIENCE, 2018, 426
  • [44] Electrochemical investigation of the influence of nitrogen alloying on pitting corrosion of austenitic stainless steels
    Jargelius-Pettersson, RFA
    CORROSION SCIENCE, 1999, 41 (08) : 1639 - 1664
  • [45] Electrochemical evaluation of cr-mn austenitic stainless steel in aqueous sulphuric acid and influence of thiocyanate ions
    Bansod, Ankur V.
    Patil, Awanikumar P.
    Shukla, Sourabh
    ANTI-CORROSION METHODS AND MATERIALS, 2020, 67 (03) : 281 - 293
  • [46] Studies on the Cooperative Influence of Cr and Mo on the Pitting Corrosion Resistance of Super Austenitic Stainless Steels
    Li, Bingbing
    Lang, Yuping
    Chen, Haitao
    Qu, Huapeng
    Feng, Hanqiu
    Sun, Xu
    Tian, Zhiling
    MATERIALS, 2023, 16 (23)
  • [47] Influence of the Alloying Elements on Pitting Corrosion of Stainless Steels: A Modeling Approach
    Malki, B.
    Souier, T.
    Baroux, B.
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2008, 155 (12) : C583 - C587
  • [48] Preparation of high nitrogen Cr-Ni and Cr-Mn stainless steel powders by mechanical alloying and their compositional dependence of austenitizing
    Miura, H
    Ogawa, H
    Omuro, K
    HIGH NITROGEN STEELS '98, 1999, 318-3 : 707 - 714
  • [49] Evaluation of the corrosion and mechanical properties of a range of experimental Cr-Mn stainless steels
    Univ of the Witwatersrand, Wits, South Africa
    Materials Science and Engineering A, 1995, A199 (02): : 183 - 194
  • [50] APPLICATION OF ANALYTICAL ELECTRON-MICROSCOPY FOR IDENTIFICATION OF MICROSTRUCTURES IN CR-MN AUSTENITIC STEELS
    SASAKI, T
    REUDL, E
    ULTRAMICROSCOPY, 1984, 12 (1-2) : 112 - 112
12345