Identification of processing parameters for Fe-15Cr-2.2Mo-15Ni-0.3Ti austenitic stainless steel using processing maps

被引:17
|
作者
Sivaprasad, PV [1 ]
Mannan, SL
Prasad, YVRK
Chaturvedi, RC
机构
[1] Indira Gandhi Ctr Atom Res, Mat Dev Grp, Kalpakkam 603102, Tamil Nadu, India
[2] Indian Inst Sci, Dept Met, Bangalore 560012, Karnataka, India
[3] Indian Inst Technol, Lucknow, Uttar Pradesh, India
关键词
D O I
10.1179/026708301101510186
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The processing parameters for hot working of Fe - 15Cr - 2.2Mo - 15Ni - 0.3Ti austenitic stainless steel (alloy D9) are identified using processing maps developed on the basis of the dynamic materials model and hot compression data in the temperature range 850-1250 degreesC and strain rate range 0.001-100 s(-1). The efficiency of power dissipation increased with increase in temperature and decrease in strain rate. Dynamically recrystallised microstructures resulted when the efficiency of power dissipation was in the range 27-37%, i,e, in the temperature range 1050 - 1250 degreesC and strain rate range 0.001 - 0.5 s(-1). Flow localisation occurred in the regions of instability at temperatures lower than 1000 degreesC and at higher strain rates. The dynamic recrystallisation regime observed in this alloy is compared with other austenitic stainless steels, namely, AISI type 304L and 316L. (C) 2001 IoM Communications Ltd.
引用
收藏
页码:545 / 550
页数:6
相关论文
共 50 条
  • [21] ACTIVATION-ENERGY FOR SERRATED FLOW IN A 15CR-15NI TI-MODIFIED AUSTENITIC STAINLESS-STEEL
    VENKADESAN, S
    PHANIRAJ, C
    SIVAPRASAD, PV
    RODRIGUEZ, P
    ACTA METALLURGICA ET MATERIALIA, 1992, 40 (03): : 569 - 580
  • [22] The effect of prior microstructure on the low cycle fatigue behaviour of a 15Cr-15Ni, Ti modified austenitic stainless steel
    Sandhya, R
    Rao, KBS
    Mannan, SL
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2005, 58 (2-3) : 303 - 308
  • [23] Processing maps for Fe-24Ni-11Cr-3Ti-1Mo superalloy
    Cai Dayong
    Zhang Chunling
    Tang Zhiguo
    Dong Haifeng
    Wang Peng
    BULLETIN OF MATERIALS SCIENCE, 2011, 34 (03) : 525 - 529
  • [24] Processing maps for Fe-24Ni-11Cr-3Ti-1Mo superalloy
    Cai D.
    Zhang C.
    Tang Z.
    Dong H.
    Wang P.
    Bulletin of Materials Science, 2011, 34 (3) : 525 - 529
  • [25] ROLE OF PHOSPHORUS IN HIGH-TEMPERATURE STRENGTH OF FE-16CR-15NI-25MO AUSTENITIC STAINLESS-STEEL
    HOSOI, Y
    WADE, N
    KAKEHI, K
    TANINO, M
    KOMATSU, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1988, 52 (07) : 685 - 693
  • [26] The relationship between work hardening and the nature of serrations observed in a 15Cr-15Ni-2.3Mo-Ti modified austenitic stainless steel during tensile testing
    Sivaprasad, PV
    Venugopal, S
    Venkadesan, S
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1999, 52 (05): : 337 - 344
  • [27] Hot Deformation Behavior and Processing Maps of 0.3C–15Cr–1Mo–0.5N High Nitrogen Martensitic Stainless Steel
    Xin Cai
    Xiao-Qiang Hu
    Lei-Gang Zheng
    Dian-Zhong Li
    Acta Metallurgica Sinica (English Letters), 2020, 33 : 693 - 704
  • [28] Creep-fatigue interaction behaviour of a 15Cr-15Ni, Ti modified austenitic stainless steel as a function of Ti/C ratio and microstructure
    Sandhya, R
    Rao, KBS
    Mannan, SL
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 392 (1-2): : 326 - 334
  • [29] Room Temperature Torsional Behavior of 15-Cr-15Ni Titanium Modified Austenitic Stainless Steel
    Mahata, Avik Kumar
    Borah, Utpal
    Davinci, Arvinth
    Albert, Shaju K.
    Ravishankar, B.
    STRUCTURAL INTEGRITY, 2014, 86 : 166 - 172
  • [30] Microstructures and mechanical properties of Fe-15% Cr-15% Ni austenitic stainless steels containing different levels of niobium additions submitted to various processing stages
    Padilha, AF
    Machado, IF
    Plaut, RL
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2005, 170 (1-2) : 89 - 96