EFFECT OF MICROPOROUS AGGREGATE ON LIGHTWEIGHT ALUMINA-MAGNESIA CASTABLE FOR LADLE

被引：0
|
作者：
Gu, H. Z. [1 ]
Huang, A. [1 ]
Zhang, M. J. [1 ]
Du, B. [2 ]
Li, Z. K. [3 ]
Wang, Q. [2 ]
Fu, L. P. [1 ]
机构：
[1] Wuhan Univ Sci & Technol, State Key Lab Breeding Base Refarctories & Ceram, Hubei Wuhan 430081, Peoples R China
[2] Zhejiang Zili Co Ltd, Zhejinag 312300, Peoples R China
[3] Jiangsu Jingxing High Temp Mat Co Ltd, Jiangsu 225265, Peoples R China
来源：
PROCEEDINGS OF THE UNIFIED INTERNATIONAL TECHNICAL CONFERENCE ON REFRACTORIES (UNITECR 2013) | 2014年
基金：
中国国家自然科学基金;
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Two kinds of self-made microporous aggregates were applied to replace the tabular corundum aggregate, alumina-magnesia castables were prepared, and effect of microporous aggregates on the properties of alumina-magnesia castable was studied. The results show that the apparent porosity of lightweight castable is higher than that of tabular corundum castable due to the decrease of bulk density (BD), however, its permanent linear change (PLC) and thermal conductivity are smaller, strength is also higher; In term of the over-all slag resistance performance, the lightweight castable with composite microporous aggregate is better.
引用
收藏
页码：692 / +
页数：3
相关论文
共 50 条
  • [31] Interaction between microporous magnesia castable and 38CrMoAl steel
    Yuan, Cheng
    Liu, Yu
    Li, Guang-qiang
    Zou, Yong-shun
    Huang, Ao
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2023, 30 (03) : 516 - 524
  • [32] Interaction between microporous magnesia castable and 38CrMoAl steel
    Cheng Yuan
    Yu Liu
    Guang-qiang Li
    Yong-shun Zou
    Ao Huang
    Journal of Iron and Steel Research International, 2023, 30 : 516 - 524
  • [33] ALUMINA-MAGNESIA-CARBON BRICKS FOR STEEL LADLE
    Klewski, Marcin
    Lucyna, Obszynska
    Michal, Sulkowski
    Proceedings of the Unified International Technical Conference on Refractories (UNITECR 2013), 2014, : 715 - 718
  • [34] How effective is the addition of nanoscaled particles to alumina-magnesia refractory castables?
    Sako, E. Y.
    Braulio, M. A. L.
    Pandolfelli, V. C.
    CERAMICS INTERNATIONAL, 2012, 38 (06) : 5157 - 5164
  • [35] Dynamic interaction of refractory and molten steel: Effect of alumina-magnesia castables on alloy steel cleanness
    Huang, Ao
    Wang, Yajie
    Gu, Huazhi
    Zou, Yongshun
    CERAMICS INTERNATIONAL, 2018, 44 (18) : 22146 - 22153
  • [36] Novel Features of Nanoscaled Particles Addition to Alumina-Magnesia Refractory Castables
    Braulio, Mariana A. L.
    Morbioli, Guilherme G.
    Bittencourt, Luis Rodolfo M.
    Pandolfelli, Victor C.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2010, 93 (09) : 2606 - 2610
  • [37] Sintering Analysis of a Fine-Grained Alumina-Magnesia Spinel Powder
    Benameur, Nassira
    Bernard-Granger, Guillaume
    Addad, Ahmed
    Raffy, Stephane
    Guizard, Christian
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 (05) : 1388 - 1396
  • [38] Expansion behavior of cement-bonded alumina-magnesia refractory castables
    Braulio, M. A. L.
    Milanez, D. H.
    Sako, E. Y.
    Bittencourt, L. R. M.
    Pandolfelli, V. C.
    AMERICAN CERAMIC SOCIETY BULLETIN, 2007, 86 (12):
  • [39] Magnesium fluoride role on alumina-magnesia cement-bonded castables
    Souza, T. M.
    Luz, A. P.
    Pandolfelli, V. C.
    CERAMICS INTERNATIONAL, 2014, 40 (09) : 14947 - 14956
  • [40] Tailoring the Microstructure of Cement-Bonded Alumina-Magnesia Refractory Castables
    Braulio, Mariana A. L.
    Pandolfelli, Victor C.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2010, 93 (10) : 2981 - 2985
12345