Mechanical properties of P/M 316L stainless steel materials

被引：87
|
作者：
Kurgan, N. [1 ]
Varol, R. [2 ]
机构：
[1] Karabuk Univ, Fac Engn, Karabuk, Turkey
[2] Bartin Univ, Fac Engn, Bartin, Turkey
来源：
POWDER TECHNOLOGY | 2010年 / 201卷 / 03期
关键词：
Powder metallurgy; 316L Stainless steel; Sintering; Mechanical property;
D O I：
10.1016/j.powtec.2010.03.041
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
In this work, 316L stainless steel (SS) powder was used. The composition of the powder is as follows: 0.015% C, 1.75% Mn, 0.45% Si, 17.24% Cr, 2.79% Mo, 14.65% Ni, and balance iron. Mixed powder was compressed cold using single action press under 800 MPa pressure. Compressed samples were sintered at 1200 degrees C, 1250 degrees C, and 1300 degrees C into the nitrogen gas atmosphere. In order to determine the mechanical properties of the produced specimens, the fatigue tests, tensile test, three-point bending test, impact test and hardness tests were applied to the specimens. Determined mechanical properties in the result of this work were compared to the properties as stated in ASTM F138-G2. Besides that to define the microstructures of the produced specimens in detail, metallographic studies were performed. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：242 / 247
页数：6
相关论文
共 50 条
  • [31] Processing and mechanical properties of porous 316L stainless steel for artificial hip joints
    Dewidar, MM
    Khalil, KA
    Hassan, MK
    Tag, G
    Seo, DW
    Lim, JK
    MULTISCALE DAMAGE RELATED TO ENVIRONMENT ASSISTED CRACKING, 2005, : 43 - 49
  • [32] Effect of nitrogen content on mechanical properties of 316L(N) austenitic stainless steel
    Wang, Yong
    Wang, Zhenhua
    Wang, Wei
    Ma, Bingyang
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 884
  • [33] The effect of repeated repair welding on mechanical and corrosion properties of stainless steel 316L
    AghaAli, Iman
    Farzam, Mansour
    Golozar, Mohammad Ali
    Danaee, Iman
    MATERIALS & DESIGN, 2014, 54 : 331 - 341
  • [34] Effect of infiltration on the mechanical properties and corrosion resistance of 316L austenitic stainless steel
    Ivanus, Radu Cristian
    METALURGIA INTERNATIONAL, 2008, 13 (03): : 39 - 45
  • [35] MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ELECTRON BEAM DEPOSITS OF AISI 316L STAINLESS STEEL
    Wang, Liang
    Felicelli, Sergio D.
    Coleman, Jacob
    Johnson, Rene
    Taminger, Karen M. B.
    Lett, Ratessiea L.
    PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION 2011, VOL 3, 2012, : 15 - 21
  • [36] Mechanical properties of 316L stainless steel fabricated by wire and arc additive manufacturing
    Zhao Y.
    Fan R.
    Liu Y.
    Wang Z.
    Jianzhu Jiegou Xuebao/Journal of Building Structures, 2023, 44 (08): : 207 - 216
  • [37] Research on mechanical properties and microstructure by selective laser melting of 316L stainless steel
    Pan Lu
    Zhang Cheng-Lin
    Wang Liang
    Liu Tong
    Li Xiao-Cheng
    MATERIALS RESEARCH EXPRESS, 2019, 6 (12)
  • [38] Gelcasting of 316L stainless steel
    Li, Yan
    Guo, Zhimeng
    Hao, Junjie
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2007, 14 (06): : 507 - 511
  • [39] Dynamic mechanical properties of 316L stainless steel fabricated by an additive manufacturing process
    Chen, Jie
    Wei, Haiyang
    Bao, Kuo
    Zhang, Xianfeng
    Cao, Yang
    Peng, Yong
    Kong, Jian
    Wang, Kehong
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 11 (11): : 170 - 179
  • [40] Microstructural evolution and mechanical properties of 316L stainless steel using multiaxial forging
    Rajput, S. K.
    Kumar, Jitendra
    Mehta, Yashwant
    Soota, Tarun
    Saxena, K. K.
    ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES, 2020, 6 (03) : 509 - 518
12345