Mechanical properties of P/M 316L stainless steel materials

被引：87

作者：

Kurgan, N. ^{[1
]}

Varol, R. ^{[2
]}

机构：

[1] Karabuk Univ, Fac Engn, Karabuk, Turkey

[2] Bartin Univ, Fac Engn, Bartin, Turkey

来源：

POWDER TECHNOLOGY | 2010年 / 201卷 / 03期

关键词：

Powder metallurgy; 316L Stainless steel; Sintering; Mechanical property;

D O I：

10.1016/j.powtec.2010.03.041

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

In this work, 316L stainless steel (SS) powder was used. The composition of the powder is as follows: 0.015% C, 1.75% Mn, 0.45% Si, 17.24% Cr, 2.79% Mo, 14.65% Ni, and balance iron. Mixed powder was compressed cold using single action press under 800 MPa pressure. Compressed samples were sintered at 1200 degrees C, 1250 degrees C, and 1300 degrees C into the nitrogen gas atmosphere. In order to determine the mechanical properties of the produced specimens, the fatigue tests, tensile test, three-point bending test, impact test and hardness tests were applied to the specimens. Determined mechanical properties in the result of this work were compared to the properties as stated in ASTM F138-G2. Besides that to define the microstructures of the produced specimens in detail, metallographic studies were performed. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：242 / 247

页数：6

共 50 条

[21] Influence of porosity on mechanical and corrosion properties of SLM 316L stainless steel
Dengcui Yang
Xinfeng Kan
Pengfei Gao
Yan Zhao
Yanjun Yin
Zhengzhi Zhao
Jiquan Sun
Applied Physics A, 2022, 128
[22] Mechanical properties of zirconia-coated 316L austenitic stainless steel
Universidade de Sao Paulo, Sao Carlos, Brazil
J Mater Sci Lett, 21 (1868-1871):
[23] Mechanical properties and microstructure of 316L stainless steel produced by hybrid manufacturing
Feldhausen, Thomas
Raghavan, Narendran
Saleeby, Kyle
Love, Lonnie
Kurfess, Thomas
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2021, 290
[24] Effect of Co Addition to Heat-Treated P/M 316L Stainless Steel on α′-Martensite Formation and Mechanical Properties
Pichaiwong, Nantawan
Wangyao, Panyawat
Lothongkum, Gobboon
Visuttipitukul, Patama
Asavavisithchai, Seksak
Tongsri, Ruangdaj
Chuankrerkkul, Nutthita
MATERIALS TESTING, 2012, 54 (11-12) : 762 - 768
[25] Effect of Cr Limits on Microstructure and Mechanical Properties of P/M 316L Austenitic Steel
Erden, Mehmet Akif
Demirtas, Hueseyin
Oleiwi, Fadhil Hussein
SCIENCE OF SINTERING, 2024, 56 (01) : 79 - 87
[26] Impact of 316L Stainless Steel on Microstructural and Mechanical Properties of AA5083/316L Metal Matrix Composites
Sekban, Dursun Murat
JOM, 2024,
[27] Effect of surface mechanical attrition treatment on microstructures and mechanical properties of 316L stainless steel
Yang, Xiao-Hua
Dui, Wei-Zhen
Liu, Gang
Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2007, 28 (02): : 118 - 121
[28] Characterization, mechanical properties and deformation behavior of highly porous materials made of titanium and stainless steel (316L)
Bram, M
Nelles, H
Buchkremer, HP
Stöver, D
MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2000, 31 (06) : 497 - 500
[29] Mechanical properties of Austenitic Stainless Steel 304L and 316L at elevated temperatures
Desu, Raghuram Karthik
Krishnamurthy, Hansoge Nitin
Balu, Aditya
Gupta, Amit Kumar
Singh, Swadesh Kumar
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2016, 5 (01): : 13 - 20
[30] Microstructure and Mechanical Properties of 316L Stainless Steel Produced by Selective Laser Melting
Qi, Xiaotong
Feng, Haoming
Liu, Lin
MATERIALS SCIENCE, ENERGY TECHNOLOGY AND POWER ENGINEERING III (MEP 2019), 2019, 2154

← 1 2 3 4 5 →