Effects of stress ratio on crack growth rate and fatigue strength for high cycle and very-high-cycle fatigue of metallic materials

被引：36

作者：

Sun, Chengqi ^{[1
]}

Lei, Zhengqiang ^{[1
]}

Hong, Youshi ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China

来源：

MECHANICS OF MATERIALS | 2014年 / 69卷 / 01期

基金：

中国国家自然科学基金;

关键词：

Stress ratio; Crack growth rate; Fatigue strength; Very-high-cycle fatigue; Metallic materials; DRIVING-FORCE PARAMETER; LOAD RATIO; PROPAGATION BEHAVIOR; STEELS; LIFE; PREDICTION; MECHANISMS; THRESHOLD; FAILURE; CLOSURE;

D O I：

10.1016/j.mechmat.2013.10.007

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This paper studies the effects of stress ratio R on crack growth rate and fatigue strength for high cycle and very-high-cycle fatigue of metallic materials. First, the effect of R on fatigue crack growth rate is analyzed, and the result shows that the effect of R on crack growth rate at near-threshold region and on Paris region is well expressed by a unified relation. Then, a model is developed for describing the fatigue crack growth rate with the effect of R in near-threshold region and Paris region. The model is verified by experimental data of metallic materials in literature. Finally, a formula is derived for the effect of R on fatigue strength. The estimated results are in good agreement with the experimental data for high cycle and very-high-cycle fatigue regime in literature. The comparison of the present result with Goodman diagram is also discussed. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：227 / 236

页数：10

共 50 条

[41] Effects of local microstructure on crack initiation in super martensitic stainless steel under very-high-cycle fatigue
Li, Xue
Dai, Yajun
Wang, Xiangyu
Liu, Yongjie
Chen, Yao
Wang, Chong
Zhang, Hong
Li, Lang
Liu, Hanqing
He, Chao
Wang, Qingyuan
INTERNATIONAL JOURNAL OF FATIGUE, 2022, 163
[42] Microstructural Influences on Very-High-Cycle Fatigue-Crack Initiation in Ti-6246
Szczepanski, C. J.
Jha, S. K.
Larsen, J. M.
Jones, J. W.
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (12): : 2841 - 2851
[43] Crack path and regularities for ball-bearing fracture in the very-high-cycle fatigue regime
Shanyavskiy, Andrey A.
Soldatenkov, Aleksey P.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (11) : 3378 - 3392
[44] Mechanism of fatigue crack initiation and propagation in the very high cycle fatigue regime of high-strength steels
Grad, P.
Reuscher, B.
Brodyanski, A.
Kopnarski, M.
Kerscher, E.
SCRIPTA MATERIALIA, 2012, 67 (10) : 838 - 841
[45] Investigations on the fatigue crack propagation threshold in Very High Cycle Fatigue
Wang, Chong
Wagner, Daniele
Bathias, Claude
11TH INTERNATIONAL FATIGUE CONGRESS, PTS 1 AND 2, 2014, 891-892 : 357 - 362
[46] Investigation of high cycle and Very-High-Cycle Fatigue behaviors for a structural steel with smooth and notched specimens
Qian, Guian
Hong, Youshi
Zhou, Chengen
ENGINEERING FAILURE ANALYSIS, 2010, 17 (7-8) : 1517 - 1525
[47] EFFECTS OF ENVIRONMENTAL MEDIA ON HIGH CYCLE AND VERY-HIGH-CYCLE FATIGUE BEHAVIORS OF STRUCTURAL STEEL 40Cr
Qian Gui'an
Hong Youshi
ACTA METALLURGICA SINICA, 2009, 45 (11) : 1356 - 1363
[48] Connection among the characteristics of the low cycle fatigue, high cycle fatigue and fatigue crack growth
Nagy, Gyula
Lukacs, Jankos
MECHANICAL BEHAVIOR OF MATERIALS X, PTS 1AND 2, 2007, 345-346 : 533 - +
[49] A novel evaluation method for high cycle and very high cycle fatigue strength
Wu, Han
Sun, Chengqi
Xu, Wei
Chen, Xin
Wu, Xiaolei
ENGINEERING FRACTURE MECHANICS, 2023, 290
[50] Microstructure refinement and grain size distribution in crack initiation region of very-high-cycle fatigue regime for high-strength alloys
Chang, Yukun
Pan, Xiangnan
Zheng, Liang
Hong, Youshi
INTERNATIONAL JOURNAL OF FATIGUE, 2020, 134 (134)

← 1 2 3 4 5 →