Effects of stress ratio on crack growth rate and fatigue strength for high cycle and very-high-cycle fatigue of metallic materials

被引：36

作者：

Sun, Chengqi ^{[1
]}

Lei, Zhengqiang ^{[1
]}

Hong, Youshi ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China

来源：

MECHANICS OF MATERIALS | 2014年 / 69卷 / 01期

基金：

中国国家自然科学基金;

关键词：

Stress ratio; Crack growth rate; Fatigue strength; Very-high-cycle fatigue; Metallic materials; DRIVING-FORCE PARAMETER; LOAD RATIO; PROPAGATION BEHAVIOR; STEELS; LIFE; PREDICTION; MECHANISMS; THRESHOLD; FAILURE; CLOSURE;

D O I：

10.1016/j.mechmat.2013.10.007

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This paper studies the effects of stress ratio R on crack growth rate and fatigue strength for high cycle and very-high-cycle fatigue of metallic materials. First, the effect of R on fatigue crack growth rate is analyzed, and the result shows that the effect of R on crack growth rate at near-threshold region and on Paris region is well expressed by a unified relation. Then, a model is developed for describing the fatigue crack growth rate with the effect of R in near-threshold region and Paris region. The model is verified by experimental data of metallic materials in literature. Finally, a formula is derived for the effect of R on fatigue strength. The estimated results are in good agreement with the experimental data for high cycle and very-high-cycle fatigue regime in literature. The comparison of the present result with Goodman diagram is also discussed. (C) 2013 Elsevier Ltd. All rights reserved.

引用

下载

页码：227 / 236

页数：10

共 50 条

[1] Effects of specimen size on fatigue life of metallic materials in high-cycle and very-high-cycle fatigue regimes
Sun, C.
Zhang, X.
Liu, X.
Hong, Y.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (06) : 770 - 779
[2] The nature and the mechanism of crack initiation and early growth for very-high-cycle fatigue of metallic materials - An overview
Hong, Youshi
Sun, Chengqi
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2017, 92 : 331 - 350
[3] Correlation of crack growth rate and stress ratio for fatigue damage containing very high cycle fatigue regime
Sun, Chengqi
Hong, Youshi
THEORETICAL AND APPLIED MECHANICS LETTERS, 2012, 2 (03)
[4] Correlation of crack growth rate and stress ratio for fatigue damage containing very high cycle fatigue regime
Chengqi Sun
Theoretical & Applied Mechanics Letters, 2012, 2 (03) : 11 - 14
[5] Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels
Hong, Youshi
Lei, Zhengqiang
Sun, Chengqi
Zhao, Aiguo
INTERNATIONAL JOURNAL OF FATIGUE, 2014, 58 : 144 - 151
[6] Fatigue Strength and Crack Initiation Mechanism of Very-High-Cycle Fatigue for Low Alloy Steels
Youshi Hong
Aiguo Zhao
Guian Qian
Chengen Zhou
Metallurgical and Materials Transactions A, 2012, 43 : 2753 - 2762
[7] Fatigue Strength and Crack Initiation Mechanism of Very-High-Cycle Fatigue for Low Alloy Steels
Hong, Youshi
Zhao, Aiguo
Qian, Guian
Zhou, Chengen
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (08): : 2753 - 2762
[8] A simulation on microstructure sensitivity to very-high-cycle fatigue behavior of metallic materials
Lei, Zhengqiang
Xie, Jijia
Zhao, Aiguo
Hong, Youshi
ISAB-2010 - FIRST INTERNATIONAL SYMPOSIUM ON ARCHIMEDES BRIDGE, 2010, 4 : 225 - 232
[9] Mechanisms of interior crack initiation in very-high-cycle fatigue of high-strength alloys
Liu, Xiaolong
Chen, Erqing
Zeng, Fan
Cong, Tao
Domblesky, Joseph P.
ENGINEERING FRACTURE MECHANICS, 2019, 212 : 153 - 163
[10] Effects of inclusion size and stress ratio on the very-high-cycle fatigue behavior of pearlitic steel
Cong, Tao
Qian, Guian
Zhang, Guanzhen
Wu, Si
Pan, Xiangnan
Du, Leiming
Liu, Xiaolong
INTERNATIONAL JOURNAL OF FATIGUE, 2021, 142

← 1 2 3 4 5 →