Evaluation of the effectiveness of treatment products in improving the quality of ceramics used in new and historical buildings

Ceramic samples made with a mixture of 70% ball clay and 30% quartz sand were moulded and then fired at 900 degrees C in an electric kiln. Samples were then treated with different products and analyses and tests were performed to evaluate the physical changes induced by the application of these products and their effects on the quality of the ceramics. A petrographic study indicated that the ceramics were composed of quartz, small amounts of mullite and sanidine and traces of hematite. Mineral clays (i.e. kaolinite) disappeared during firing. Two consolidating products (Paraloid B72 and Tegovakon V) and one water repellent (Silo 111) were applied to samples by capillarity, and physical changes (colour, water flow, porosity and pore size distribution) were measured. Finally, we carried out salt crystallization tests in order to determine which product improved the quality of the ceramics. Treated samples registered a decrease in porosity and a general increase in pore size. The application of Silo 111 drastically reduced water absorption by immersion and by capillarity. This product was also responsible for a decrease in pore interconnection. Samples treated with Tegovakon V performed better in terms of their overall hydric behaviour. Silo 111 was the only product that did not modify the colour of samples when compared with untreated ones, and after accelerated aging tests, samples treated with this product hindered the absorption of saline solution into ceramic pores and prevented their decay. Paraloid B72 did not improve any of the properties of the ceramics. (C) 2012 Elsevier Masson SAS. All rights reserved.