Hydrogen-induced cracking of an alumina ceramic

被引：6
|
作者：
Shi, B [1 ]
Su, YJ [1 ]
Qiao, LJ [1 ]
Chu, WY [1 ]
机构：
[1] Univ Sci & Technol Beijing, Dept Mat Phys, Beijing 100083, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE LETTERS | 2001年 / 20卷 / 22期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1023/A:1013590024462
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The possibility of hydrogen-induced cracking (HIC) of alumina ceramic during cathodic charging under constant load was studied. HIC was compared to stress corrosion cracking (SCC) in water. It was found that hydrogen could enter into alumina ceramic during cathodic charging and HIC occurred during charging under constant load.
引用
收藏
页码：2047 / 2048
页数：2
相关论文
共 50 条
  • [41] Hydrogen-induced cracking by nanovoids in 310 stainless steel
    Huang, Yizhong
    Chen, Qizhi
    Wang, Yanbin
    Chu, Wuyang
    Science China Series E Technological Sciences, 1998, 41 (04): : 372 - 382
  • [42] Mechanism of hydrogen-induced intergranular cracking of tubular steels
    乔利杰
    褚武扬
    于广华
    程以环
    Science in China(Series E:Technological Sciences), 1996, (05) : 543 - 550
  • [43] Hydrogen-induced cracking by nanovoids in 310 stainless steel
    Yizhong Huang
    Qizhi Chen
    Yanbin Wang
    Wuyang Chu
    Science in China Series E: Technological Sciences, 1998, 41 : 372 - 382
  • [44] Hydrogen-Induced Cracking of Welded Truss Gusset Plates
    William F. Jones
    Journal of Failure Analysis and Prevention, 2022, 22 : 2082 - 2086
  • [45] Hydrogen-Induced Cracking of Welded Truss Gusset Plates
    Jones, William F., III
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2022, 22 (05) : 2082 - 2086
  • [46] HYDROGEN-INDUCED CRACKING IN FESI SINGLE-CRYSTALS
    WANG, YB
    CHU, WY
    HSIAO, CM
    CORROSION, 1988, 44 (01) : 14 - 21
  • [47] In situ TEM study on hydrogen-induced cracking of nickel
    Li, J.
    Wang, Y.
    Qiao, L.
    Chu, W.
    Jinshu Xuebao/Acta Metallurgica Sinica, 2001, 37 (09): : 911 - 916
  • [48] Effect of microstructure on hydrogen-induced cracking of linepipe steels
    Koh, S. U.
    Jung, H. G.
    Kang, K. B.
    Park, G. T.
    Kim, K. Y.
    CORROSION, 2008, 64 (07) : 574 - 585
  • [49] Fracture Caused by Hydrogen-Induced Cold Cracking.
    Moeser, Martin
    1600, (35):
  • [50] Hydrogen blistering and hydrogen-induced cracking in amorphous nickel phosphorus coating
    Zhou, Q. J.
    Qiao, L. J.
    Qi, H. B.
    Li, J. X.
    He, J. Y.
    Chu, W. Y.
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2007, 353 (44-46) : 4011 - 4014
12345