Hydrogen-induced cracking of an alumina ceramic

被引：6
|
作者：
Shi, B [1 ]
Su, YJ [1 ]
Qiao, LJ [1 ]
Chu, WY [1 ]
机构：
[1] Univ Sci & Technol Beijing, Dept Mat Phys, Beijing 100083, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE LETTERS | 2001年 / 20卷 / 22期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1023/A:1013590024462
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The possibility of hydrogen-induced cracking (HIC) of alumina ceramic during cathodic charging under constant load was studied. HIC was compared to stress corrosion cracking (SCC) in water. It was found that hydrogen could enter into alumina ceramic during cathodic charging and HIC occurred during charging under constant load.
引用
收藏
页码：2047 / 2048
页数：2
相关论文
共 50 条
  • [21] Hydrogen-induced cracking and blistering in steels: A review
    Martin, May L.
    Sofronis, Petros
    JOURNAL OF NATURAL GAS SCIENCE AND ENGINEERING, 2022, 101
  • [22] Hydrogen-induced delayed fracture of alumina ceramics
    Shi, B
    Su, YJ
    Qiao, LJ
    Chu, WY
    ACTA METALLURGICA SINICA, 2001, 37 (09) : 932 - 934
  • [23] Hydrogen-induced delayed fracture of alumina ceramics
    Shi, B.
    Su, Y.
    Qiao, L.
    Chu, W.
    Jinshu Xuebao/Acta Metallurgica Sinica, 2001, 37 (09): : 932 - 934
  • [24] Acoustic Emission Monitoring of Wet H 2 S Cracking of Linepipe Steels: Application to Hydrogen-Induced Cracking and Stress-Oriented Hydrogen-Induced Cracking
    Smanio, V.
    Kittel, J.
    Fregonese, M.
    Cassagne, T.
    Normand, B.
    Ropital, F.
    CORROSION, 2011, 67 (06)
  • [25] Hydrogen-induced cracking by nanovoids in 310 stainless steel
    Department of Material Physics, Univ. of Sci. and Technology Beijing, Beijing 100083, China
    Sci China Ser E Technol Sci, 4 (x5-382):
  • [26] Hydrogen-induced cracking behaviors of Incoloy alloy 825
    Yang, Yong-jin
    Gao, Ke-wei
    Chen, Chang-feng
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2010, 17 (01) : 58 - 62
  • [27] Hydrogen-induced cracking behaviors of Incoloy alloy 825
    Yong-jin Yang
    Ke-wei Gao
    Chang-feng Chen
    International Journal of Minerals, Metallurgy, and Materials, 2010, 17 : 58 - 62
  • [28] Effects of microstructure on hydrogen-induced cracking in aluminum alloys
    Ben Ali, N.
    Tanguy, D.
    Estevez, R.
    SCRIPTA MATERIALIA, 2011, 65 (03) : 210 - 213
  • [29] DYNAMIC-MODEL OF HYDROGEN-INDUCED INTERGRANULAR CRACKING
    KAMEDA, J
    JOKL, ML
    SCRIPTA METALLURGICA, 1982, 16 (03): : 325 - 330
  • [30] In situ TEM study on hydrogen-induced cracking of nickel
    Li, JX
    Wang, YB
    Qiao, LJ
    Chu, WY
    ACTA METALLURGICA SINICA, 2001, 37 (09) : 911 - 916
12345