Hydrogen-induced cracking of an alumina ceramic

被引：6
|
作者：
Shi, B [1 ]
Su, YJ [1 ]
Qiao, LJ [1 ]
Chu, WY [1 ]
机构：
[1] Univ Sci & Technol Beijing, Dept Mat Phys, Beijing 100083, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE LETTERS | 2001年 / 20卷 / 22期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1023/A:1013590024462
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The possibility of hydrogen-induced cracking (HIC) of alumina ceramic during cathodic charging under constant load was studied. HIC was compared to stress corrosion cracking (SCC) in water. It was found that hydrogen could enter into alumina ceramic during cathodic charging and HIC occurred during charging under constant load.
引用
收藏
页码：2047 / 2048
页数：2
相关论文
共 50 条
  • [1] Stress corrosion cracking and hydrogen-induced cracking of an alumina ceramic
    Shi, B
    Chu, WY
    Su, YJ
    Gao, KW
    Qiao, LJ
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2005, 88 (02) : 353 - 356
  • [2] Hydrogen-induced cracking
    不详
    MATERIALS PERFORMANCE, 2004, 43 (11) : 55 - 55
  • [3] Controlling Hydrogen-Induced Cracking
    Guy, Blaine
    WELDING JOURNAL, 2013, 92 (09) : 82 - 84
  • [4] Hydrogen-Induced Delayed Cracking
    Pohl, M.
    PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2019, 56 (09): : 556 - 566
  • [5] DISCUSSION OF HYDROGEN-INDUCED COLD CRACKING
    BONISZEW.T
    GRANJON, MH
    THURSTON, HG
    MURRAY, JD
    SMITH, N
    BAGNALL, BI
    LINDBORG, U
    BAKER, RG
    LEIDE, NG
    VARGA, T
    BAILEY, N
    LEE, EH
    EVANS, GM
    HEWITT, J
    BOLER, R
    SCHNADT, H
    METAL CONSTRUCTION AND BRITISH WELDING JOURNAL, 1969, 1 (2SI): : 109 - &
  • [6] Hydrogen-induced cracking in titanium alloys
    Nozue, A
    Endo, K
    Tateishi, S
    Okubo, T
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1998, 62 (04) : 358 - 362
  • [7] HYDROGEN-INDUCED CRACKING IN PURE IRON
    ARMSTRONG, JH
    CARPENTER, SH
    JOURNAL DE PHYSIQUE, 1985, 46 (C-10): : 139 - 142
  • [8] Hydrogen-induced cracking and blistering in α-brass
    Panagopoulos, CN
    El-Amoush, AS
    Agathocleous, PE
    CORROSION SCIENCE, 1998, 40 (11) : 1837 - 1844
  • [9] Common misconceptions about hydrogen-induced cracking
    Moore, EM
    McIntyre, DR
    MATERIALS PERFORMANCE, 1998, 37 (10) : 77 - 81
  • [10] Hydrogen-induced cracking of commercial purity titanium
    Clarke, CF
    Hardie, D
    Ikeda, BM
    CORROSION SCIENCE, 1997, 39 (09) : 1545 - 1559
12345