Microstructure and Mechanical Properties of Two-Phase Cr-Cr2Ta Alloys

被引：23

作者：

Bhowmik, Ayan ^{[1
]}

Stone, Howard J. ^{[1
]}

机构：

[1] Univ Cambridge, Dept Mat Sci & Met, Rolls Royce UTC, Cambridge CB2 3QZ, England

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2012年 / 43A卷 / 09期

基金：

英国工程与自然科学研究理事会;

关键词：

C15 LAVES PHASE; TI-CR ALLOYS; FRACTURE-BEHAVIOR; TEST TEMPERATURE; NB; STRENGTH; DEFORMATION; CHROMIUM; RESISTANCE; STABILITY;

D O I：

10.1007/s11661-012-1140-6

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The microstructure and fracture toughness values of a series of binary Cr-Cr2Ta alloys have been studied in the as-cast condition and after long-term annealing of up to 500 hours at 1573 K (1300 A degrees C). With increasing annealing time, both the Cr(Ta) solid solution and the Cr2Ta Laves phases progressively approached equilibrium compositions. This observation was accompanied by the transformation of the Laves phase from the hexagonal C14 to the cubic C15 polytype, along with a small fraction of an intermediate hexagonal polytype. The overall hardness values of the alloys increased with the Laves phase fraction, which was accompanied by a decrease in the room-temperature fracture toughness values. The fracture surface of the three-point bend specimens revealed brittle cleavage-type fracture in all the alloys.

引用

页码：3283 / 3292

页数：10

共 50 条

[41] Microstructure and mechanical properties of rapidly solidified Al-Cr alloys
Guofa Mi
Yalin Mo
Kuangfei Wang
Journal of Wuhan University of Technology-Mater. Sci. Ed., 2009, 24 : 424 - 427
[42] Effects of Cr on the microstructure and mechanical properties of WCoB base hard alloys
Komai, Masao
Isobe, Yoshihiko
Takagi, Ken-ichi
Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, 1993, 40 (01): : 38 - 43
[43] Microstructure and Mechanical Properties of Rapidly Solidified Al-Cr Alloys
米国发
Journal of Wuhan University of Technology(Materials Science Edition), 2009, 24 (03) : 424 - 427
[44] Microstructure and Mechanical Properties of Rapidly Solidified Al-Cr Alloys
米国发
Journal of Wuhan University of Technology(Materials Science), 2009, 24 (03) : 424 - 427
[45] Co-deformation of two-phase Cu-Cr alloys
Sinclair, CW
Embury, JD
Weatherly, GC
Conlon, KT
PHILOSOPHICAL MAGAZINE, 2005, 85 (26-27) : 3137 - 3156
[46] Oxidation of two-phase Cu-Cr alloys with different microstructures
Fu, GY
Niu, Y
Wu, WT
Guan, HR
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2001, 11 (03) : 333 - 336
[47] Oxidation of two-phase Cu-Cr alloys with different microstructures
付广艳
牛焱
吴维
管恒荣
Transactions of Nonferrous Metals Society of China, 2001, (03) : 333 - 336
[48] Effects of alloy additions on the microstructure and properties of Cr-Cr2Nb alloys
Liu, C.T.
Tortorelli, P.F.
Horton, J.A.
Carmichael, C.A.
Materials Science and Engineering A, 1996, A214 (1-2): : 23 - 32
[49] Effects of alloy additions on the microstructure and properties of Cr-Cr2Nb alloys
Liu, CT
Tortorelli, PF
Horton, JA
Carmichael, CA
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 214 (1-2): : 23 - 32
[50] Microstructure and Mechanical Properties of Cr2Nb-Based Laves Phase Alloys Prepared by Laser Surface Remelting
Li, K. W.
Li, S. M.
Wang, X. B.
Zhong, H.
Xue, Y. L.
Fu, H. Z.
JOM, 2014, 66 (09) : 1886 - 1892

← 1 2 3 4 5 →