Microstructure and Mechanical Properties of Two-Phase Cr-Cr2Ta Alloys

被引：23
|
作者：
Bhowmik, Ayan [1 ]
Stone, Howard J. [1 ]
机构：
[1] Univ Cambridge, Dept Mat Sci & Met, Rolls Royce UTC, Cambridge CB2 3QZ, England
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2012年 / 43A卷 / 09期
基金：
英国工程与自然科学研究理事会;
关键词：
C15 LAVES PHASE; TI-CR ALLOYS; FRACTURE-BEHAVIOR; TEST TEMPERATURE; NB; STRENGTH; DEFORMATION; CHROMIUM; RESISTANCE; STABILITY;
D O I：
10.1007/s11661-012-1140-6
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructure and fracture toughness values of a series of binary Cr-Cr2Ta alloys have been studied in the as-cast condition and after long-term annealing of up to 500 hours at 1573 K (1300 A degrees C). With increasing annealing time, both the Cr(Ta) solid solution and the Cr2Ta Laves phases progressively approached equilibrium compositions. This observation was accompanied by the transformation of the Laves phase from the hexagonal C14 to the cubic C15 polytype, along with a small fraction of an intermediate hexagonal polytype. The overall hardness values of the alloys increased with the Laves phase fraction, which was accompanied by a decrease in the room-temperature fracture toughness values. The fracture surface of the three-point bend specimens revealed brittle cleavage-type fracture in all the alloys.
引用
收藏
页码：3283 / 3292
页数：10
相关论文
共 50 条
  • [31] Microstructure and Mechanical Properties of Laves Phase-strengthened Fe-Cr-Zr Alloys
    Tan, L.
    Yang, Y.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2015, 46A (03): : 1188 - 1195
  • [32] Microstructure and Mechanical Properties of Laves Phase-strengthened Fe-Cr-Zr Alloys
    L. Tan
    Y. Yang
    Metallurgical and Materials Transactions A, 2015, 46 : 1188 - 1195
  • [33] Microstructure and mechanical properties of Laves phase-reinforced Fe-Zr-Cr alloys
    Scudino, S.
    Donnadieu, P.
    Surreddi, K. B.
    Nikolowski, K.
    Stoica, M.
    Eckert, J.
    INTERMETALLICS, 2009, 17 (07) : 532 - 539
  • [34] Effect of Ru additions on microstructure and mechanical properties of Cr-TaCr2 alloys
    Tien, RH
    Zhu, JH
    Liu, CT
    Walker, LR
    INTERMETALLICS, 2005, 13 (3-4) : 361 - 366
  • [35] Effects of Ta on Microstructure and Mechanical Properties of Novel γ+γ' Two-Phase Ir-based Superalloys
    Ta元素对新型γ+γ'双相Ir基高温合金显微组织和力学性能的影响
    Yang, Jieren (yangjieren@nwpu.edu.cn), 1600, Science Press (49):
  • [36] HEAT TREATMENTS OF TWO-PHASE TITANIUM ALLOYS, CORRELATIONS BETWEEN MICROSTRUCTURE AND MECHANICAL PROPERTIES
    Morri, A.
    METALLURGIA ITALIANA, 2008, (11-12): : 19 - 28
  • [37] Heat treatments of two-phase titanium alloys, correlations between microstructure and mechanical properties
    Morri, A.
    Metallurgia Italiana, 2008, 100 (10):
  • [38] Effects of Fe additions on the mechanical properties and oxidation behavior of Cr2Ta Laves phase reinforced Cr
    Brady, MP
    Liu, CT
    Zhu, JH
    Tortorelli, PF
    Walker, LR
    SCRIPTA MATERIALIA, 2005, 52 (09) : 815 - 819
  • [39] Microstructure and mechanical properties of rapidly solidified Al-Cr alloys
    Mi Guofa
    Mo Yalin
    Wang Kuangfei
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2009, 24 (03): : 424 - 427
  • [40] Microstructure and mechanical properties of Ti-Zr-Cr biomedical alloys
    Wang, Pan
    Feng, Yan
    Liu, Fengchao
    Wu, Lihong
    Guan, Shaokang
    MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2015, 51 : 148 - 152
12345