Properties of Iodine-Doped CdTe Layers on (211) Si Grown at High Substrate Temperatures by MOVPE

被引：1
|
作者：
Niraula, M. [1 ]
Yasuda, K. [1 ]
Torii, R. [1 ]
Higashira, Y. [1 ]
Tamura, R. [1 ]
Chaudhari, B. S. [1 ]
Kobayashi, T. [1 ]
Goto, H. [1 ]
Fujii, S. [1 ]
Agata, Y. [1 ]
机构：
[1] Nagoya Inst Technol, Grad Sch Engn, Showa Ku, Nagoya, Aichi 4668555, Japan
来源：
JOURNAL OF ELECTRONIC MATERIALS | 2020年 / 49卷 / 11期
关键词：
CdTe epilayers; iodine doping; high substrate temperature; Si substrate; doping mechanism;
D O I：
10.1007/s11664-020-08420-3
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
The properties of iodine-doped (211) CdTe layers grown on (211) Si substrates by metalorganic vapor-phase epitaxy at high substrate temperatures from 325 degrees C to 450 degrees C were studied. The growth rate of the doped layer increased with increasing substrate temperature before reaching a maximum value of 2.6 mu m/h at 425 degrees C, after which it decreased slightly. On the other hand, the room-temperature electron density showed a strong dependence on the Te/Cd precursor flow-rate ratios, where the electron density increased with a decreasing Te/Cd ratio. The highest electron density of 2.5x10(18)cm(-3)was obtained by growing the epilayer at a substrate temperature of 400 degrees C and Te/Cd ratio of 0.05. This was considered to be due to decreased donor compensation at a small Te/Cd ratio. Good correspondence was observed between the results obtained from Hall measurements and photoluminescence measurements.
引用
收藏
页码：6996 / 6999
页数：4
相关论文
共 50 条
  • [21] Development of Nuclear Radiation Detectors by Use of Thick Single-Crystal CdTe Layers Grown on (211) p+-Si Substrates by MOVPE
    K. Yasuda
    M. Niraula
    Y. Wajima
    H. Yamashita
    N. Takai
    Y. Suzuki
    M. Matsumoto
    Y. Tsukamoto
    Y. Tsukamoto
    Y. Agata
    Journal of Electronic Materials, 2014, 43 : 2860 - 2863
  • [22] Development of Nuclear Radiation Detectors by Use of Thick Single-Crystal CdTe Layers Grown on (211) p+-Si Substrates by MOVPE
    Yasuda, K.
    Niraula, M.
    Wajima, Y.
    Yamashita, H.
    Takai, N.
    Suzuki, Y.
    Matsumoto, M.
    Tsukamoto, Y.
    Tsukamoto, Y.
    Agata, Y.
    JOURNAL OF ELECTRONIC MATERIALS, 2014, 43 (08) : 2860 - 2863
  • [23] Dark Current Characteristics of a Radiation Detector Array Developed Using MOVPE-Grown Thick CdTe Layers on Si Substrate
    K. Yasuda
    M. Niraula
    N. Fujimura
    T. Tachi
    H. Inuzuka
    S. Namba
    S. Muramatsu
    T. Kondo
    Y. Agata
    Journal of Electronic Materials, 2012, 41 : 2754 - 2758
  • [24] Dark Current Characteristics of a Radiation Detector Array Developed Using MOVPE-Grown Thick CdTe Layers on Si Substrate
    Yasuda, K.
    Niraula, M.
    Fujimura, N.
    Tachi, T.
    Inuzuka, H.
    Namba, S.
    Muramatsu, S.
    Kondo, T.
    Agata, Y.
    JOURNAL OF ELECTRONIC MATERIALS, 2012, 41 (10) : 2754 - 2758
  • [25] HIGH-RESOLUTION PHOTOLUMINESCENCE STUDIES OF (211) CDTE GROWN ON (211)B GAAS SUBSTRATE
    CHEN, SD
    LIN, L
    HE, XZ
    XU, ZY
    LUO, CP
    XU, JZ
    JOURNAL OF CRYSTAL GROWTH, 1994, 140 (3-4) : 287 - 290
  • [26] Structural properties of Si-doped β-Ga2O3 layers grown by MOVPE
    Gogova, D.
    Wagner, G.
    Baldini, M.
    Schmidbauer, M.
    Irmscher, K.
    Schewski, R.
    Galazka, Z.
    Albrecht, M.
    Fornari, R.
    JOURNAL OF CRYSTAL GROWTH, 2014, 401 : 665 - 669
  • [27] Shadow donor magnetospectroscopy in MBE: Grown CdTe layers doped with indium and iodine
    Karpierz, K
    Lusakowski, J
    Szot, M
    Romanowski, Z
    Karczewski, G
    Grynberg, M
    PHYSICA STATUS SOLIDI B-BASIC RESEARCH, 1998, 210 (02): : 783 - 786
  • [28] Dislocation Density Reduction in MOVPE-Grown (211) CdTe/Si by Post-Growth Patterning and Annealing
    Chaudhari, B. S.
    Niraula, M.
    Takagi, Y.
    Okumura, R.
    Sharma, K. P.
    Maruyama, T.
    JOURNAL OF ELECTRONIC MATERIALS, 2023, 52 (05) : 3431 - 3435
  • [29] Dislocation Density Reduction in MOVPE-Grown (211) CdTe/Si by Post-Growth Patterning and Annealing
    B. S. Chaudhari
    M. Niraula
    Y. Takagi
    R. Okumura
    K. P. Sharma
    T. Maruyama
    Journal of Electronic Materials, 2023, 52 : 3431 - 3435
  • [30] Growth condition of iodine-doped n+-CdTe layers in metal-organic vapor phase epitaxy
    Yasuda, K
    Tomita, Y
    Masuda, Y
    Ishiguro, T
    Kawauchi, Y
    Morishita, H
    Agata, Y
    JOURNAL OF ELECTRONIC MATERIALS, 2002, 31 (07) : 785 - 790
12345