INHIBITORY ACTION OF GARLIC EXTRACT IN THE CORROSION OF COPPER UNDER THIN ELECTROLYTE LAYERS

被引：3

作者：

Chen, Zhenyu ^{[1
,2
]}

Cen, Hongyu ^{[1
]}

Wei, Lisha ^{[1
]}

Cao, Yamin ^{[1
]}

Guo, Xingpeng ^{[1
,2
]}

机构：

[1] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Minist Educ, Key Lab Mat Chem Energy Convers & Storage, Wuhan 430074, Hubei, Peoples R China

[2] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Hubei Key Lab Mat Chem & Serv Failure, Wuhan 430074, Hubei, Peoples R China

来源：

SURFACE REVIEW AND LETTERS | 2019年 / 26卷 / 01期

基金：

中国国家自然科学基金;

关键词：

Garlic extracts; atmospheric corrosion; inhibitor; XPS; X-RAY PHOTOELECTRON; ORGANOSULFUR CONSTITUENTS; ATMOSPHERIC CORROSION; CARBON-STEEL; SURFACE; SPECTROSCOPY; RESPONSES; BEHAVIOR; PHASE; OIL;

D O I：

10.1142/S0218625X18501287

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The inhibition effects of garlic extract on copper corrosion under a thin electrolyte layer (TEL) were investigated using weight-loss measurements, electrochemical methods and surface analysis. Results showed that the volatile organosulfur compounds of garlic extract, such as diallyl trisulfide and di-2-propenyl disulfide, among others, could adsorb on the surface of copper and have a significant inhibitory effect on copper corrosion. Garlic extract acted as a mixed-type inhibitor for copper under TEL. Surface analyses, such as scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS), were conducted to illustrate the inhibitive mechanisms of this plant extract under a TEL.

引用

页数：9

共 50 条

[41] Low cycle fatigue of thin aluminium and copper layers and their susceptibility to corrosion
Sebastian, Breitenreiner
Nadine, Pfluegler
Reinhard, Pufall
Bernhard, Wunderle
2022 IEEE 9TH ELECTRONICS SYSTEM-INTEGRATION TECHNOLOGY CONFERENCE, ESTC, 2022, : 545 - 552
[42] Corrosion behavior of Mg-10Gd-2Y-0.4Zr alloy under thin electrolyte layers
Chen, C.
Zhang, T.
Meng, G.
Shao, Y.
Wang, F.
Li, X.
Dong, C.
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2010, 61 (05): : 388 - 397
[43] Corrosion inhibitory action of leaves of Mussaenda Frondosa Extract on controlling corrosion of carbon steel in well water
Pradeep, X. Joy
Sathiyabama, J.
MATERIALS TODAY-PROCEEDINGS, 2021, 47 : 326 - 331
[44] Corrosion Behaviour of Copper under the Action of Chlorine-containing Thin Liquid Film and Aspergillus Versicolor
Feng Y.-L.
Li X.-M.
Zhao Y.
Yao Q.
Zou S.-W.
Xiao K.
Surface Technology, 2022, 51 (09): : 178 - 187
[45] INHIBITORY ACTION OF PYRIDINE-DERIVATIVES ON CORROSION OF COPPER IN POTASSIUM PERSULFATE SOLUTIONS
PATEL, NK
FRANCO, J
PATEL, KC
CHIMICA & L INDUSTRIA, 1975, 57 (01): : 10 - 12
[46] Inhibitory action of 3-trimethoxysilylpropanethiol-1 on copper corrosion in NaCl solutions
Beccaria, AM
Bertolotto, C
ELECTROCHIMICA ACTA, 1997, 42 (09) : 1361 - 1371
[47] TIME DEPENDENCE OF COPPER AND TIN COATED COPPER CORROSION UNDER STEAM ACTION
Badea, Gabriela Elena
Badea, Teodora
UNIVERSITY POLITEHNICA OF BUCHAREST SCIENTIFIC BULLETIN SERIES B-CHEMISTRY AND MATERIALS SCIENCE, 2006, 68 (01): : 17 - 24
[48] Unveiling the interaction between corrosion products and oxygen reduction on the corrosion of Mg-4Nd-0.4Zr alloy under thin electrolyte layers
Dan, Ningning
Yang, Yao
Ying, Tao
Zeng, Xiaoqin
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2025, 222 : 195 - 214
[49] On the atmospheric corrosion of metals which are covered with thin electrolyte layers. III. The measurement of polarisation curves on metal surfaces which are covered by thin electrolyte layers
Stratmann, M.
Streckel, H.
Kim, K.T.
Crockett, S.
1600, (30): : 6 - 7
[50] ON THE ATMOSPHERIC CORROSION OF METALS WHICH ARE COVERED WITH THIN ELECTROLYTE LAYERS .3. THE MEASUREMENT OF POLARIZATION CURVES ON METAL-SURFACES WHICH ARE COVERED BY THIN ELECTROLYTE LAYERS
STRATMANN, M
STRECKEL, H
KIM, KT
CROCKETT, S
CORROSION SCIENCE, 1990, 30 (6-7) : 715 - 734

← 1 2 3 4 5 →