INHIBITORY ACTION OF GARLIC EXTRACT IN THE CORROSION OF COPPER UNDER THIN ELECTROLYTE LAYERS

被引：3
|
作者：
Chen, Zhenyu [1 ,2 ]
Cen, Hongyu [1 ]
Wei, Lisha [1 ]
Cao, Yamin [1 ]
Guo, Xingpeng [1 ,2 ]
机构：
[1] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Minist Educ, Key Lab Mat Chem Energy Convers & Storage, Wuhan 430074, Hubei, Peoples R China
[2] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Hubei Key Lab Mat Chem & Serv Failure, Wuhan 430074, Hubei, Peoples R China
来源：
SURFACE REVIEW AND LETTERS | 2019年 / 26卷 / 01期
基金：
中国国家自然科学基金;
关键词：
Garlic extracts; atmospheric corrosion; inhibitor; XPS; X-RAY PHOTOELECTRON; ORGANOSULFUR CONSTITUENTS; ATMOSPHERIC CORROSION; CARBON-STEEL; SURFACE; SPECTROSCOPY; RESPONSES; BEHAVIOR; PHASE; OIL;
D O I：
10.1142/S0218625X18501287
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The inhibition effects of garlic extract on copper corrosion under a thin electrolyte layer (TEL) were investigated using weight-loss measurements, electrochemical methods and surface analysis. Results showed that the volatile organosulfur compounds of garlic extract, such as diallyl trisulfide and di-2-propenyl disulfide, among others, could adsorb on the surface of copper and have a significant inhibitory effect on copper corrosion. Garlic extract acted as a mixed-type inhibitor for copper under TEL. Surface analyses, such as scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS), were conducted to illustrate the inhibitive mechanisms of this plant extract under a TEL.
引用
收藏
页数：9
相关论文
共 50 条
  • [1] Models for Corrosion of Metals under Thin Electrolyte Layers
    Venkatraman, M. S.
    Bosco, I. G.
    Cole, I. S.
    Emmanuel, B.
    CORROSION (GENERAL) - 219TH ECS MEETING, 2011, 35 (17): : 1 - 10
  • [2] Corrosion of pure magnesium under thin electrolyte layers
    Zhang, Tao
    Chen, Chongmu
    Shao, Yawei
    Meng, Guozhe
    Wang, Fuhui
    Li, Xiaogang
    Dong, Chaofang
    ELECTROCHIMICA ACTA, 2008, 53 (27) : 7921 - 7931
  • [3] Benzotriazole as a volatile corrosion inhibitor during the early stage of copper corrosion under adsorbed thin electrolyte layers
    Chen, Zhenyu
    Huang, Ling
    Zhang, Guoan
    Qiu, Yubing
    Guo, Xingpeng
    CORROSION SCIENCE, 2012, 65 : 214 - 222
  • [4] Inhibitory action of aqueous garlic peel extract on the corrosion of carbon steel in HCl solution
    de Assuncao Araujo Pereira, Simone Santana
    Pegas, Michelle Macedo
    Fernandez, Tatiana Lopez
    Magalhaes, Mariana
    Schoentag, Thais Gadiole
    Lago, Dalva Cristina
    de Senna, Lilian Ferreira
    D'Elia, Eliane
    CORROSION SCIENCE, 2012, 65 : 360 - 366
  • [5] The corrosion of tin under thin electrolyte layers containing chloride
    Zhong, Xiankang
    Zhang, Guoan
    Qiu, Yubin
    Chen, Zhenyu
    Guo, Xingpeng
    Fu, Chaoyang
    CORROSION SCIENCE, 2013, 66 : 14 - 25
  • [6] Corrosion behavior of 907 steel under thin electrolyte layers of artificial seawater
    王慧萍
    丁少春
    朱娟
    张昭
    张鉴清
    曹楚南
    Journal of Central South University, 2015, 22 (03) : 806 - 814
  • [7] Corrosion behavior of 907 steel under thin electrolyte layers of artificial seawater
    Wang Hui-ping
    Ding Shao-chun
    Zhu Juan
    Zhang Zhao
    Zhang Jian-qing
    Cao Chu-nan
    JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2015, 22 (03) : 806 - 814
  • [8] Corrosion of aluminum alloy 7A04 under thin electrolyte layers
    Zhou, Herong
    Li, Xiaogang
    Dong, Chaofang
    Xiao, Kui
    Feng, Hao
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2008, 30 (08): : 880 - 887
  • [9] Advanced laboratory study on the atmospheric corrosion of zinc under thin electrolyte layers
    El-Mahdy, GA
    CORROSION, 2003, 59 (06) : 505 - 510
  • [10] Corrosion behavior of 907 steel under thin electrolyte layers of artificial seawater
    Hui-ping Wang
    Shao-chun Ding
    Juan Zhu
    Zhao Zhang
    Jian-qing Zhang
    Chu-nan Cao
    Journal of Central South University, 2015, 22 : 806 - 814
12345