Corrosion properties of surface-modified AZ91D magnesium alloy

被引：82
|
作者：
He Meifeng [1 ]
Liu Lei [1 ]
Wu Yating [1 ]
Tang Zhixin [1 ]
Hu Wenbin [1 ]
机构：
[1] Shanghai Jiao Tong Univ, State Key Lab Metal Matrix Composites, Shanghai 200030, Peoples R China
来源：
CORROSION SCIENCE | 2008年 / 50卷 / 12期
关键词：
Magnesium; Molten salts; Polarization; EIS;
D O I：
10.1016/j.corsci.2008.09.034
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Samples of AZ91D magnesium alloy were dipped into AlCl3-NaCl molten salt at different temperatures between 250 degrees C and 400 degrees C for 28800 s. The thickness of the alloying layer is increased with the rise of the treatment temperatures. The coating was mainly composed of Al12Mg17 and Al3Mg2 intermetallic compounds. The corrosion resistance of the coating which is obtained at 300 degrees C for 28800 s is the best, When the treatment temperature is higher than 300 degrees C, some cracks developed in the alloying layers. The cracks were resulted from the thermal stress due to the different thermal expansion coefficient of the AZ91D substrate and the alloying coating during the rapid cooling process. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：3267 / 3273
页数：7
相关论文
共 50 条
  • [21] Atmospheric corrosion of field-exposed magnesium alloy AZ91D
    Jonsson, Martin
    Persson, Dan
    Leygraf, Christofer
    CORROSION SCIENCE, 2008, 50 (05) : 1406 - 1413
  • [22] Corrosion resistance of aged die cast magnesium alloy AZ91D
    Song, GL
    Bowles, AL
    StJohn, DH
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 366 (01): : 74 - 86
  • [23] Anodisation of AZ91D magnesium alloy in molybdate solution for corrosion protection
    Lopez, A. D. Forero
    Lehr, I. L.
    Saidman, S. B.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 702 : 338 - 345
  • [24] Improvement of corrosion resistance of AZ91D magnesium alloy by gadolinium addition
    Zhou Xue-hua
    Wei Zhong-ling
    Chen Qiu-rong
    Gan Fu-xing
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 : S1664 - S1668
  • [25] CORROSION MECHANISM AND MODEL OF ANODIZED FILM ON AZ91D MAGNESIUM ALLOY
    Li, Lina
    Qian, Jiangang
    Lu, Zhaozhong
    Sun, Zhongwu
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2010, 24 (15-16): : 3077 - 3082
  • [26] Corrosion Fatigue Behaviour of a Common AZ91D Magnesium Alloy in Modified Simulated Body Fluid
    Jafari, Sajjad
    Raman, R. K. Singh
    11TH INTERNATIONAL FATIGUE CONGRESS, PTS 1 AND 2, 2014, 891-892 : 267 - 272
  • [27] Improvement of corrosion resistance of AZ91D magnesium alloy by gadolinium addition
    周学华
    卫中领
    陈秋荣
    甘复兴
    TransactionsofNonferrousMetalsSocietyofChina, 2006, (S3) : 1664 - 1668
  • [28] Evaluation of microstructural effects on corrosion behaviour of AZ91D magnesium alloy
    Ambat, R
    Aung, NN
    Zhou, W
    CORROSION SCIENCE, 2000, 42 (08) : 1433 - 1455
  • [29] Influence of Zeolite Coating on the Corrosion Resistance of AZ91D Magnesium Alloy
    Banerjee, P. Chakraborty
    Woo, Ren Ping
    Grayson, Sam Matthew
    Majumder, Amrita
    Raman, R. K. Singh
    MATERIALS, 2014, 7 (08) : 6092 - 6104
  • [30] Improvement of corrosion resistance of AZ91D magnesium alloy by holmium addition
    Zhou Xuehua
    Huang Yuanwei
    Wei Zhongling
    Chen Qiurong
    Gan Fuxing
    CORROSION SCIENCE, 2006, 48 (12) : 4223 - 4233
12345