Corrosion properties of surface-modified AZ91D magnesium alloy

被引：82
|
作者：
He Meifeng [1 ]
Liu Lei [1 ]
Wu Yating [1 ]
Tang Zhixin [1 ]
Hu Wenbin [1 ]
机构：
[1] Shanghai Jiao Tong Univ, State Key Lab Metal Matrix Composites, Shanghai 200030, Peoples R China
来源：
CORROSION SCIENCE | 2008年 / 50卷 / 12期
关键词：
Magnesium; Molten salts; Polarization; EIS;
D O I：
10.1016/j.corsci.2008.09.034
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Samples of AZ91D magnesium alloy were dipped into AlCl3-NaCl molten salt at different temperatures between 250 degrees C and 400 degrees C for 28800 s. The thickness of the alloying layer is increased with the rise of the treatment temperatures. The coating was mainly composed of Al12Mg17 and Al3Mg2 intermetallic compounds. The corrosion resistance of the coating which is obtained at 300 degrees C for 28800 s is the best, When the treatment temperature is higher than 300 degrees C, some cracks developed in the alloying layers. The cracks were resulted from the thermal stress due to the different thermal expansion coefficient of the AZ91D substrate and the alloying coating during the rapid cooling process. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：3267 / 3273
页数：7
相关论文
共 50 条
  • [11] Mechanical properties of thixomolded AZ91D magnesium alloy
    Zhang, Y. F.
    Liu, Y. B.
    Cao, Z. Y.
    Zhang, Q. Q.
    Zhang, L.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (03) : 1375 - 1384
  • [12] Study on corrosion resistance of AZ91D magnesium alloy ingots
    Lin, G.-Y.
    Peng, D.-S.
    Zhang, H.
    Zhao, Y.-W.
    Kuangye Gongcheng/Mining and Metallurgical Engineering, 2001, 21 (03): : 79 - 81
  • [13] EFFECTS OF Ce ON CORROSION RESISTANCE OF AZ91D MAGNESIUM ALLOY
    Z.H. Huang
    Acta Metallurgica Sinica(English Letters), 2005, (02) : 129 - 136
  • [14] About some corrosion mechanisms of AZ91D magnesium alloy
    Ballerini, G
    Bardi, U
    Bignucolo, R
    Ceraolo, G
    CORROSION SCIENCE, 2005, 47 (09) : 2173 - 2184
  • [15] Corrosion behavior of AZ91D magnesium alloy in city atmosphere
    Lin, C
    Li, XG
    Li, M
    Wang, FP
    ACTA METALLURGICA SINICA, 2004, 40 (02) : 191 - 196
  • [16] The effect of electromagnetic stirring on the microstructure and corrosion of mischmetal modified AZ91D magnesium alloy
    Jin, Y. X.
    Hua, L.
    Xu, X.
    Peng, Q.
    MATERIALS SCIENCE-POLAND, 2009, 27 (01): : 171 - 185
  • [17] Corrosion and mechanical properties of AZ91D magnesium alloy fabricated by solid recycling process
    Chino, Y
    Kishihara, R
    Shimojima, K
    Yamada, Y
    Wen, C
    Iwasaki, H
    Mabuchi, M
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2001, 65 (07) : 621 - 626
  • [18] Effect of heat treatment on microstructures and corrosion properties of SLM AZ91D magnesium alloy
    Cui B.-S.
    Wang J.-G.
    Zhang X.
    Feng Z.-H.
    Yang G.
    Yue Y.-F.
    Li J.-H.
    Surface Technology, 2021, 50 (03) : 323 - 329
  • [19] Surface oxidation of molten AZ91D magnesium alloy in air
    Balart, M. J.
    Fan, Z.
    INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2014, 27 (03) : 167 - 175
  • [20] Surface modification of AZ91D magnesium alloy by laser cladding
    Takagi, Tohru
    Shibata, Hiroki
    Kamado, Shigeharu
    Kojima, Yo
    Hiraga, Hitoshi
    Inoue, Takashi
    Keikinzoku/Journal of Japan Institute of Light Metals, 2001, 51 (11): : 619 - 624
12345