Effect of heat-treatment on crystalline phase and UV absorption of 60CeO2-40TiO2 thin films by magnetron sputtering

60CeO(2)-40TiO(2) thin films were deposited on soda-lime silicate glass substrates by R.F. magnetron sputtering. The effects of heat-treatment on the UV-absorption of the thin films were studied on the 60CeO(2)-40TiO(2) thin film with the largest UV cut-off wavelength. The sample films with CeO2:TiO2=60:40 were heated at 773 K, 873 K, 973 K for 30 min. These films are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy and spectrometer (XPS). XRD analysis proves that the addition of TiO2 to CeO2 changed the crystalline state of CeO2. But the UV absorption effect of CeO2-TiO2 films with CeO2 crystallite phase is inferior to that of the amorphous phase CeO2-TiO2 films. XPS analysis also indicates that the amorphous phase CeO2-TiO2 films have the most Ce3+ content in these films. Amorphous phase and crystalline phase of the CeO2-TiO2 films have different effects on UV absorption of the thin films.