Interface structure and mechanical properties of the TiAl/42CrMo steel joint vacuum brazed with Ag-Cu/Ti/Ag-Cu filler metal

被引：50
|
作者：
Li, Yulong [1 ]
He, Peng [1 ]
Feng, Jicai [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
来源：
SCRIPTA MATERIALIA | 2006年 / 55卷 / 02期
关键词：
TiAl; brazing; interface structure; mechanical properties;
D O I：
10.1016/j.scriptamat.2006.03.055
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
TiAl and 42CrMo steel were vacuum brazed with Ag-Cu/Ti/Ag-Cu filler metal. The joint interface was divided into three distinct zones, including the reaction layer near TiAl, the central zone, and the TiC reaction layer adjacent to the steel. During brazing, AlCu2Ti, AlCuTi and TiC phase formed quickly with an increase in brazing temperature or brazing time. By comparing the brazing conditions and joint strengths, the optimum brazing parameters were obtained. When brazed at 900 degrees C for 5 min, the room temperature tensile strength and shear strength of the joint were 347 MPa and 229 MPa, respectively. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：171 / 174
页数：4
相关论文
共 50 条
  • [41] Corrosion Behavior of Ti6Al4V/Al2O3 Vacuum Brazed Joints with Ag-Cu Eutectic Filler
    Alves, A. C.
    Ariza, E.
    Guedes, A.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
  • [42] EFFECT OF ADDITIONAL ELEMENTS IN AG-CU BASED FILLER METAL ON BRAZING OF ALUMINUM NITRIDE TO METALS
    KUZUMAKI, T
    ARIGA, T
    MIYAMOTO, Y
    ISIJ INTERNATIONAL, 1990, 30 (12) : 1135 - 1141
  • [43] Setting and flexural properties of metal-resin composite using Ag-Cu particles as filler and chemical accelerator
    Soma, H
    Miyagawa, Y
    Ogura, H
    DENTAL MATERIALS JOURNAL, 2003, 22 (04) : 543 - 555
  • [44] Brazing ZTA ceramic to TC4 alloy using Ag-Cu filler metal
    Wang X.
    Cao J.
    Dai X.
    Feng J.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (03): : 47 - 51and58
  • [45] Effect of joining temperature and holding time on microstructure and shear strength of Ti2AlC/Cu joints brazed using Ag-Cu filler alloy
    Zhang, J.
    Wang, G. C.
    Hea, Y. M.
    Sun, Y.
    He, X. D.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 567 : 58 - 64
  • [46] Microstructure and mechanical properties of Al2O3 ceramic and TiAl alloy joints brazed with Ag-Cu-Ti filler metal
    Niu, G. B.
    Wang, D. P.
    Yang, Z. W.
    Wang, Y.
    CERAMICS INTERNATIONAL, 2016, 42 (06) : 6924 - 6934
  • [47] Characterizing the Decomposition of Ti2AlC during its Brazing with Cu by Using Ag-Cu Filler Alloy
    Wang, Guochao
    Zhang, Jie
    Liu, Xiaowen
    PHYSICAL AND NUMERICAL SIMULATION OF MATERIALS PROCESSING VII, 2013, 762 : 607 - +
  • [48] Microstructure and Mechanical Property of Titanium Film-Modified Sapphire/High Nb-TiAl Alloy Joints Using Ag-Cu Filler by Vacuum Brazing
    Chen, S. F.
    Wang, Y. S.
    Sun, D. B.
    Xing, X. G.
    Gao, J.
    Hei, H. J.
    Wang, Y. L.
    Yu, S. W.
    Lin, J. P.
    JOM, 2024, 76 (12) : 7304 - 7314
  • [49] Effect of calcium on the microstructure and mechanical properties of brazed joint using Ag-Cu-Zn brazing filler metal
    Sui, Fangfei
    Long, Weimin
    Liu, Shengxin
    Zhang, Guanxing
    Bao, Li
    Li, Hao
    Chen, Yong
    MATERIALS & DESIGN, 2013, 46 : 605 - 608
  • [50] Joining Alumina to Titanium Alloys Using Ag-Cu Sputter-Coated Ti Brazing Filler
    Emadinia, Omid
    Guedes, Anibal
    Tavares, Carlos Jose
    Simoes, Sonia
    MATERIALS, 2020, 13 (21) : 1 - 14
12345