The Effect of Flue Gas Environment on the Corrosion Behavior of the Sulfuric Acid Dew-Point Corrosion Resistant Steel

In order to compare the corrosion resistance of conventional low carbon steel, Cu containing low carbon steel for sulfuric acid dew-point corrosion inhibition, and stainless 409L, immersion tests were carried out in 50 wt.% sulfuric acid. The effects of HCl concentraion on the corrosion behavior in a fixed sulfuric acid concentration (16.9 vol.%) was also investigated by immersion test. In addition to immersion test, field test in a thermal plant was carried out for 10 months. As a result, it was confirmed that Cu-containing dew-point corrosion resistent steel has the highest corrosion resistance compared with other materials. To verify superior corrosion resistence of dew-point corrosion resistant steel, surface morpology after various test was observed by SEM. It was found that surface corroded product of the dew-point corrosion resistant steel was much denser and thicker compared with the other steel.