Enhancement of photoluminescence properties of CaAl2Si2O8:Eu2+ by SiO2 addition

被引：7

作者：

Kim, B. S. ^{[1
]}

Song, Y. H. ^{[1
]}

Jo, D. S. ^{[1
]}

Abe, T. ^{[2
]}

Senthil, K. ^{[1
]}

Masaki, T. ^{[1
]}

Toda, K. ^{[2
]}

Yoon, D. H. ^{[1
,3
]}

机构：

[1] Sungkyunkwan Univ, Sch Adv Mat Sci & Engn, Suwon 440746, South Korea

[2] Niigata Univ, Fac Engn, Dept Chem & Chem Engn, Niigata 9502181, Japan

[3] Sungkyunkwan Univ, SKKU Adv Inst Nanotechnol SAINT, Suwon 440746, South Korea

来源：

MATERIALS RESEARCH BULLETIN | 2012年 / 47卷 / 10期

关键词：

Optical materials; X-ray diffraction; Luminescence; Optical properties; LIGHT-EMITTING-DIODES; LUMINESCENT PROPERTIES; OPTICAL-PROPERTIES; PHOSPHOR; GREEN; EMISSION;

D O I：

10.1016/j.materresbull.2012.04.109

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

SiO2 added phosphors, CaAl2Si2O8:Eu2+ + xSiO(2) (x = 0, 1, 2, 3, 4, 5, 6 and 13 mol) were synthesized by a novel liquid phase precursor (LPP) method. The photoluminescence properties of phosphor added by 5 mol of SiO2 showed 110% enhancement in the emission intensity compared to the CaAl2Si2O8:Eu2+ phosphor. A broad emission and excitation wavelength was observed approximately from 400 nm to 600 nm centered at 430 nm and from 280 nm to 400 nm centered at 365 nm, respectively. Photoluminescence intensity of the phosphors increased continuously by SiO2 addition up to x = 5 mol and then it decreased with further addition of SiO2. The observed photoluminescence properties of the phosphors were discussed related to their crystalline structure and morphology. (C) 2012 Elsevier Ltd. All rights reserved.

引用

页码：3015 / 3019

页数：5

共 50 条

[21] Structure and photoluminescence characteristics of europium(III) doped in CaAl2Si2O8 phosphors
Dai, W. B.
Zhou, M.
Xian, Z. Y.
Zeng, L. K.
RSC ADVANCES, 2014, 4 (49): : 25470 - 25478
[22] Mechanism of the reduction and energy transfer between Eu2+ and Eu3+ in Eu-doped CaAl2Si2O8 materials prepared in air
Dai, W. B.
JOURNAL OF MATERIALS CHEMISTRY C, 2014, 2 (20) : 3951 - 3959
[23] CaAl2Si2O8 polymorphs: Sensitive geothermometers and geospeedometers
Gorelova, Liudmila A.
Vereshchagin, Oleg S.
Bocharov, Vladimir N.
Krivovichev, Sergey V.
Zolotarev, Andrey A.
Rassomakhin, Mikhail A.
GEOSCIENCE FRONTIERS, 2023, 14 (01)
[24] Degree of polymerization of the CaAl2Si2O8 aluminosilicate glass
Kuryaeva, R. G.
GLASS PHYSICS AND CHEMISTRY, 2006, 32 (05) : 505 - 510
[25] STRUCTURAL STUDIES ON PURE ANORTHITE CAAL2SI2O8
KALUS, CK
ACTA CRYSTALLOGRAPHICA SECTION A, 1978, 34 : S29 - S29
[26] Degree of polymerization of the CaAl2Si2O8 aluminosilicate glass
R. G. Kuryaeva
Glass Physics and Chemistry, 2006, 32 : 505 - 510
[27] Persistent luminescence in CaAl2Si2O8:Eu2+, R3+ (R = Pr, Nd, Dy, Ho and Er)
Ju, Guifang
Hu, Yihua
Chen, Li
Wang, Xiaojuan
Mu, Zhongfei
JOURNAL OF LUMINESCENCE, 2014, 146 : 102 - 108
[28] NUCLEATION, GROWTH AND STABILITY OF CAAL2SI2O8 POLYMORPHS
ABE, T
TSUKAMOTO, K
SUNAGAWA, I
PHYSICS AND CHEMISTRY OF MINERALS, 1991, 17 (06) : 473 - 484
[29] THE 10-PERCENT CAAL2SI2O8 PLANE IN THE SYSTEM CASIO3-CA2AL2SIO7-NAALSIO4-CAAL2SI2O8
YODER, HS
JOURNAL OF GEOLOGY, 1952, 60 (06): : 586 - 593
[30] Preparation and Spectroscopic Characteristics of CaAl2Si2O8 : Eu, Ce, Tb Fluorescent Material
Xu Dan-zhi
Feng Jing
Yang Xiao-yun
Zu En-dong
Cui Xiao-ying
Lin Jin-chang
Dong Kun
SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37 (06) : 1804 - 1808

← 1 2 3 4 5 →