Fracture of U-notched specimens under mixed mode: Experimental results and numerical predictions

被引：95
|
作者：
Gomez, F. J. [1 ]
Elices, M. [1 ]
Berto, F. [2 ]
Lazzarin, P. [2 ]
机构：
[1] Univ Politecn Madrid, Dept Mat Sci, E-28040 Madrid, Spain
[2] Univ Padua, Dept Management & Engn, I-36100 Vicenza, Italy
来源：
ENGINEERING FRACTURE MECHANICS | 2009年 / 76卷 / 02期
关键词：
Notched components; Mixed mode loading; Rupture; Cohesive crack; Notch radius; COHESIVE CRACK; SHARP NOTCHES; STRAIN-ENERGY; ELASTIC-MATERIALS; FAILURE CRITERIA; BRITTLE-FRACTURE; INITIATION; VOLUME; COMPONENTS; ELEMENTS;
D O I：
10.1016/j.engfracmech.2008.10.001
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The first part of the paper gives an account of 153 fracture tests on blunted notched specimens (with notches of root radius ranging from 0.3 to 4.0 mm), loaded under mixed mode (ranging from almost pure mode I to mode II, and beyond). Maximum loads and initial crack angles were measured as a function of notch root radius and loading mixity. Such results can help in evaluating numerical models of the fracture of notched components. The second part of the paper deals with the suitability of the cohesive crack concept for predicting fracture loads under mixed mode. Use of local mode I was considered for numerical computations. Comparison of experimental results with numerical predictions was significantly accurate. Diagrams of fracture loci for notched components loaded under mixed mode are discussed. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：236 / 249
页数：14
相关论文
共 50 条
  • [31] EFFECT OF HYDROGEN ON FRACTURE OF U-NOTCHED BEND SPECIMENS OF QUENCHED AND TEMPERED ALSL4340 STEEL
    LEE, TD
    GOLDENBERG, T
    HIRTH, JP
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (04): : 439 - 448
  • [32] Application of EMC-J criterion to fracture prediction of U-notched polymeric specimens with nonlinear behaviour
    Majidi, Hamid Reza
    Razavi, Seyed Mohammad Javad
    Torabi, Ali Reza
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2019, 42 (01) : 352 - 362
  • [33] Investigation of ductile rupture in U-notched Al 6061-T6 plates under mixed mode loading
    Torabi, A. R.
    Habibi, R.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (05) : 551 - 565
  • [34] Fracture of PBX notched specimens: Experimental research and numerical prediction
    Liu, Y. L.
    Cendon, D. A.
    Chen, P. W.
    Dai, K. D.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2017, 90 : 268 - 275
  • [35] Mixed mode fracture of double-edge notched specimens of concrete
    Gálvez, JC
    Cendón, DA
    Elices, M
    FRACTURE MECHANICS OF CONCRETE STRUCTURES, VOLS 1 AND 2, 2001, : 349 - 356
  • [36] Fracture Load Predictions in Short Glass Fiber Reinforced Polyamide 6 U-Notched Specimens Combining the Equivalent Material Concept and the Theory of Critical Distances
    Cicero, S.
    Torabi, A. R.
    Ibanez-Guderrez, F. T.
    Azizi, P.
    JOURNAL OF TESTING AND EVALUATION, 2020, 48 (02) : 1226 - 1251
  • [37] Mixed mode fracture: numerical evaluation and experimental validation using PMMA specimens
    Pereira, Sergio A. G.
    Tavares, Sergio M. O.
    de Castro, Paulo M. S. T.
    FRATTURA ED INTEGRITA STRUTTURALE, 2019, 13 (49): : 412 - 428
  • [38] Application of the equivalent material concept to fracture of U-notched solids under small scale yielding
    Gomez, F. J.
    Torabi, A. R.
    ECF22 - LOADING AND ENVIRONMENTAL EFFECTS ON STRUCTURAL INTEGRITY, 2018, 13 : 267 - 272
  • [39] Fracture in PMMA notched specimens under compression - Experimental study
    Bura, Elzbieta
    Derpenski, Lukasz
    Seweryn, Andrzej
    POLYMER TESTING, 2019, 77
  • [40] Fracture of V-notched specimens under mixed mode (I + II) loading in brittle materials
    F. J. Gómez
    M. Elices
    F. Berto
    P. Lazzarin
    International Journal of Fracture, 2009, 159 : 121 - 135
12345