Fracture of U-notched specimens under mixed mode: Experimental results and numerical predictions

被引：95
|
作者：
Gomez, F. J. [1 ]
Elices, M. [1 ]
Berto, F. [2 ]
Lazzarin, P. [2 ]
机构：
[1] Univ Politecn Madrid, Dept Mat Sci, E-28040 Madrid, Spain
[2] Univ Padua, Dept Management & Engn, I-36100 Vicenza, Italy
来源：
ENGINEERING FRACTURE MECHANICS | 2009年 / 76卷 / 02期
关键词：
Notched components; Mixed mode loading; Rupture; Cohesive crack; Notch radius; COHESIVE CRACK; SHARP NOTCHES; STRAIN-ENERGY; ELASTIC-MATERIALS; FAILURE CRITERIA; BRITTLE-FRACTURE; INITIATION; VOLUME; COMPONENTS; ELEMENTS;
D O I：
10.1016/j.engfracmech.2008.10.001
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The first part of the paper gives an account of 153 fracture tests on blunted notched specimens (with notches of root radius ranging from 0.3 to 4.0 mm), loaded under mixed mode (ranging from almost pure mode I to mode II, and beyond). Maximum loads and initial crack angles were measured as a function of notch root radius and loading mixity. Such results can help in evaluating numerical models of the fracture of notched components. The second part of the paper deals with the suitability of the cohesive crack concept for predicting fracture loads under mixed mode. Use of local mode I was considered for numerical computations. Comparison of experimental results with numerical predictions was significantly accurate. Diagrams of fracture loci for notched components loaded under mixed mode are discussed. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：236 / 249
页数：14
相关论文
共 50 条
  • [21] Fracture assessment of graphite V-notched and U-notched specimens by using the cohesive crack model
    Cendon, D. A.
    Torabi, A. R.
    Elices, M.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2015, 38 (05) : 563 - 573
  • [22] Experimental verification of two stress-based criteria for mixed mode I/III brittle fracture assessment of U-notched components
    Saboori, Behnam
    Torabi, A. R.
    Ayatollahi, M. R.
    Berto, F.
    ENGINEERING FRACTURE MECHANICS, 2017, 182 : 229 - 244
  • [23] Averaged strain energy density to assess mixed mode I/III fracture of U-notched GPPS samples
    Saboori, Behnam
    Torabi, A. R.
    Berto, F.
    Razavi, S. M. J.
    STRUCTURAL ENGINEERING AND MECHANICS, 2018, 65 (06) : 699 - 706
  • [24] DUCTILE FRACTURE OF U-NOTCHED BEND SPECIMENS OF SPHEROIDIZED AISI-1095 STEEL
    GOLDENBERG, T
    LEE, TD
    HIRTH, JP
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (11): : 1663 - 1671
  • [25] Estimation of Mode I Fracture of U-Notched Polycarbonate Specimens Using the Equivalent Material Concept and Strain Energy Density
    Albinmousa, Jafar
    AlSadah, Jihad
    Hawwa, Muhammad A.
    Al-Qahtani, Hussain M.
    APPLIED SCIENCES-BASEL, 2021, 11 (08):
  • [26] Prevalent mode II fracture assessment of inclined U-notched specimens made of tungsten-copper functionally graded material
    Mohammadi, H.
    Salavati, H.
    Alizadeh, Y.
    Berto, F.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2017, 89 : 90 - 99
  • [27] Experimental research and numerical modelling of mode I fracture initiation in notched polycarbonate specimens
    Bura, Elzbieta
    Augustyniak, Jakub
    Seweryn, Andrzej
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2025, 138
  • [28] Compressive fracture analysis of U-notched specimens made of porous graphite reinforced by aluminum particles
    Torabi, A. R.
    Hamidi, Kazem
    Shahbazian, B.
    DIAMOND AND RELATED MATERIALS, 2021, 120
  • [29] EFFECT OF HYDROGEN ON FRACTURE OF U-NOTCHED BEND SPECIMENS OF SPHEROIDIZED AISI-1095 STEEL
    LEE, TD
    GOLDENBERG, T
    HIRTH, JP
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (02): : 199 - 208
  • [30] Observation of mixed mode fracture with center notched disk specimens
    Jia, Z
    CastroMontero, A
    Shah, SP
    CEMENT AND CONCRETE RESEARCH, 1996, 26 (01) : 125 - 137
12345