Fatigue initiation and propagation in natural and synthetic rubbers

被引:107
|
作者
Legorju-jago, K [1 ]
Bathias, C [1 ]
机构
[1] Conservatoire Natl Arts & Metiers, ITMA, Dept Mech Engn, F-75003 Paris, France
关键词
rubbers; fatigue; complex loading;
D O I
10.1016/S0142-1123(01)00062-7
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Elastomeric matrix composites are usually reinforced by mineral particles such as carbon black and sometimes by long metallic or organic fibers. In the absence of Fiber, rubbers can be considered as nanocomposites. In service conditions, the fatigue damage of rubbers is a combination of: (a) mechanical damage; (b) chemical damage; (c) thermal damage. Experience shows that, in cyclic loading, rubbers are damaged to the point of formation of one or several cracks which then propagate. As for metal, it is recommended to study separately initiation of cracks and then their propagation. Generally speaking, the fatigue resistance is affected by chemical transformation such as crystallisation. It means that compression loading is an important factor. To show this effect, an axisymetric hour-glass shape specimen (D=25 mm) is proposed to test rubbers. A large effect has been found of the mean stress on the fatigue strength depending on the chemical composition of the materials and of crystallisation transformation if it appears. The crack growth rate is studied using linear fracture mechanics as proposed earlier (Rivlin RS, Thomas AG. Rupture of rubber: I. Characteristic energy for tearing. J Polymer Sci 1953;10(3):291). In this case, the strain energy release rate G is substituted for the concept of tearing energy T. The application of fracture mechanics to elastomers generates some difficulties because of the important deformability. In order to apply a tens ion-compression loading a thick edge notched specimen is recommended with two lateral grooves (W=150 mm, B=25 mm). For low values of DeltaT, a threshold can de defined depending on the R ratio. It is shown that for a high R ratio the fatigue crack would not propagate if the crystallisation transformation is high. In contrast, if R=-1, the threshold disappears. A finite element simulation of stresses and strains is presented in order to get a better explanation of the experimental results. (C) 2002 Published by Elsevier Science Ltd.
引用
收藏
页码:85 / 92
页数:8
相关论文
共 50 条
  • [41] Fatigue crack initiation and propagation in sandwich structure
    Luo B.-L.
    Zhu Y.-F.
    Li Z.-D.
    Zheng S.-W.
    Chuan Bo Li Xue/Journal of Ship Mechanics, 2019, 23 (08): : 988 - 996
  • [42] INITIATION AND PROPAGATION OF FATIGUE CRACKS IN A CORROSIVE ENVIRONMENT
    MILLER, NA
    NEW ZEALAND JOURNAL OF SCIENCE, 1970, 13 (04): : 553 - &
  • [43] FATIGUE CRACK INITIATION AND PROPAGATION IN BONDED SHEETS
    FUNABASHI, N
    MURA, T
    KEER, LM
    JOURNAL OF ADHESION, 1978, 9 (03): : 229 - 235
  • [44] Corrosion fatigue crack initiation and crack propagation
    Dickson, JI
    ENVIRONMENTALLY INDUCED CRACKING OF METALS, PROCEEDINGS, 2000, : 3 - 5
  • [45] FUNDAMENTALS OF FATIGUE CRACK INITIATION and PROPAGATION: A REVIEW
    Pande, C. S.
    Imam, M. A.
    Srivatsan, T. S.
    FATIGUE OF MATERIALS: ADVANCES AND EMERGENCES IN UNDERSTANDING, 2010, : 3 - 18
  • [46] MECHANISMS OF CRACK INITIATION AND PROPAGATION IN CORROSION FATIGUE
    DUQUETTE, DJ
    CORROSION, 1977, 33 (04) : 151 - 151
  • [47] Fatigue crack initiation and propagation in an α-iron polycrystal
    Chu, RQ
    Cai, Z
    Li, SX
    Wang, ZG
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 313 (1-2): : 64 - 68
  • [48] Initiation and Propagation of Fatigue in Turbine Chromium Steels
    Hajkova, Pavlina
    Janovec, Jiri
    Siegl, Jan
    Smola, Bohumil
    CHEMICKE LISTY, 2011, 105 : S603 - S605
  • [49] INITIATION AND PROPAGATION OF FRETTING FATIGUE CRACKS - REPLY
    ENDO, K
    GOTO, H
    WEAR, 1977, 43 (02) : 269 - 270
  • [50] Synthetic rubbers
    Longstreth, B
    INDUSTRIAL AND ENGINEERING CHEMISTRY, 1940, 32 : 1156 - 1156