Acoustic emission study of fatigue crack closure of physical short and long cracks for aluminum alloy LY12CZ

被引：56

作者：

Chang, H. ^{[1
]}

Han, E. H. ^{[1
]}

Wang, J. Q. ^{[1
]}

Ke, W. ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Environm Corros Ctr, Shenyang 110016, Peoples R China

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2009年 / 31卷 / 03期

关键词：

Crack Closure; Physical short crack; Acoustic emission; Aluminum alloy LY12CZ; FINITE-ELEMENT-ANALYSIS; THRESHOLD;

D O I：

10.1016/j.ijfatigue.2008.08.008

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Crack closure of physical short and long cracks of LY12CZ aluminum alloy during fatigue process was investigated using acoustic emission (AE) technique. Results showed that the effective fatigue crack growth curve (da/dN vs. Delta K(eff)) of physical short and long cracks obtained by the AE technique was consistent with the effective fatigue crack growth Curve at high stress ratio (R = 0.8), which implied that the AE technique Could measure the crack closure level, especially for physical short crack. The growth rate of physical short crack was Much higher than that of long crack at the same Delta K, and the lower crack Closure level of short crack was the main reason. (C) 2008 Elsevier Ltd. All rights reserved.

引用

页码：403 / 407

页数：5

共 50 条

[21] ON THE DEVELOPMENT OF CRACK CLOSURE AND THE THRESHOLD CONDITION FOR SHORT AND LONG FATIGUE CRACKS IN 7150 ALUMINUM-ALLOY
ZAIKEN, E
RITCHIE, RO
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (08): : 1467 - 1477
[22] Mesoscopic study of ductile fracture of aluminium alloy LY12CZ
Li, T
Wang, QY
Yuan, XM
ADVANCES IN FRACTURE AND FAILURE PREVENTION, PTS 1 AND 2, 2004, 261-263 : 45 - 50
[23] Influence of cathodic polarization on corrosion fatigue life of aluminium alloy LY12CZ
Chang, H
Han, EH
Wang, JQ
Ke, W
ACTA METALLURGICA SINICA, 2005, 41 (05) : 556 - 560
[24] Effects of Laser Shock Processing on Residual Stresses of Aluminum Alloy LY12CZ
Kong Dejun
Zhu Wei
Lu Jinzhong
RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 308 - 311
[25] Corrosion behavior of LY12CZ aluminum alloy in simulated acid rain solution
An, BG
Zhang, XY
Song, SZ
Li, HX
Han, EH
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2003, 13 (01) : 116 - 120
[26] Corrosion behavior of LY12CZ aluminum alloy in simulated acid rain solution
安百刚
张学元
宋诗哲
李洪锡
韩恩厚
TransactionsofNonferrousMetalsSocietyofChina, 2003, (01) : 116 - 120
[27] Corrosion Parameters Distribution Rule and Influence Factors of LY12CZ Aluminum Alloy
Mu, Zhitao
Zhu, Zuotao
Chen, Dinghai
Ye, Bin
MANUFACTURING ENGINEERING AND AUTOMATION I, PTS 1-3, 2011, 139-141 : 321 - +
[28] Effect of Interactive Periods to Corrosion-Fatigue Life on LY12CZ Alloy
Zhang Haiwei
He Yuting
Liu Chao
Wu Liming
Ding Hua
MECHANICAL, MATERIALS AND MANUFACTURING ENGINEERING, PTS 1-3, 2011, 66-68 : 96 - +
[29] Study of transient current for a LY12CZ aluminum alloy in 3.5%NaCl solution at constant potential
Zhang, B
Li, J
Wang, JQ
Zheng, YL
Ke, W
FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, : 2341 - 2346
[30] A new method for welding aluminum alloy LY12CZ sheet with high strength
徐文立
田锡唐
刘雪松
方洪渊
China Welding, 2001, (02) : 51 - 56

← 1 2 3 4 5 →