Acoustic emission study of fatigue crack closure of physical short and long cracks for aluminum alloy LY12CZ

被引：56
|
作者：
Chang, H. [1 ]
Han, E. H. [1 ]
Wang, J. Q. [1 ]
Ke, W. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Environm Corros Ctr, Shenyang 110016, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2009年 / 31卷 / 03期
关键词：
Crack Closure; Physical short crack; Acoustic emission; Aluminum alloy LY12CZ; FINITE-ELEMENT-ANALYSIS; THRESHOLD;
D O I：
10.1016/j.ijfatigue.2008.08.008
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Crack closure of physical short and long cracks of LY12CZ aluminum alloy during fatigue process was investigated using acoustic emission (AE) technique. Results showed that the effective fatigue crack growth curve (da/dN vs. Delta K(eff)) of physical short and long cracks obtained by the AE technique was consistent with the effective fatigue crack growth Curve at high stress ratio (R = 0.8), which implied that the AE technique Could measure the crack closure level, especially for physical short crack. The growth rate of physical short crack was Much higher than that of long crack at the same Delta K, and the lower crack Closure level of short crack was the main reason. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：403 / 407
页数：5
相关论文
共 50 条
  • [1] Corrosion fatigue crack propagation behavior of LY12CZ aluminum alloy
    Huang, X. G.
    Han, Z. Y.
    Feng, G. T.
    ADVANCED MATERIALS, MECHANICAL AND STRUCTURAL ENGINEERING, 2016, : 17 - 21
  • [2] The effect of fretting on fatigue lifetime of aluminum alloy LY12CZ
    Yang, M.-S. (msyang7667@126.com), 1600, Science Press (32):
  • [3] Prediction of Fretting Fatigue Life of Aluminum Alloy LY12CZ
    Yang, Maosheng
    Chen, Yueliang
    Bi, Yuquan
    Jiang, Wenhao
    ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 : 252 - 256
  • [4] Acoustic emission study of corrosion fatigue crack propagation mechanism for LY12CZ and 7075-T6 aluminum alloys
    H. Chang
    E. Han
    J. Q. Wang
    W. Ke
    Journal of Materials Science, 2005, 40 : 5669 - 5674
  • [5] Acoustic emission study of corrosion fatigue crack propagation mechanism for LY12CZ and 7075-T6 aluminum alloys
    Chang, H
    Han, E
    Wang, JQ
    Ke, W
    JOURNAL OF MATERIALS SCIENCE, 2005, 40 (21) : 5669 - 5674
  • [6] Analysis of modal acoustic emission signals of LY12CZ aluminum alloy at anodic and cathodic polarization
    Chang, H
    Han, EH
    Wang, JQ
    Ke, W
    NDT & E INTERNATIONAL, 2006, 39 (01) : 8 - 12
  • [7] Study of corrosion fatigue for LY12CZ aluminum alloy riveted lap-splice joints
    Zhang, Bo
    Zhang, Zhenggui
    Han, Enhou
    Li, Jin
    Ke, Wei
    Jinshu Xuebao/Acta Metallurgica Sinica, 2000, 36 (08): : 842 - 846
  • [8] Probabilistic Study on Corrosion Damage Distribution and Fatigue Lives of LY12CZ Aluminum Alloy Structure
    Yu, Dazhao
    Chen, Yueliang
    Yong, Zhang
    Fan Qinghe
    MECHANICAL, MATERIALS AND MANUFACTURING ENGINEERING, PTS 1-3, 2011, 66-68 : 594 - +
  • [9] An approach to correlate fatigue crack growth rate with S-N curve for an aluminum alloy LY12CZ
    Hou, Shanqin
    Xu, Jinquan
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2018, 95 : 177 - 185
  • [10] Small-crack growth and life prediction for LY12cz aluminum clad alloy
    Wu, XR
    Yu, H
    ADVANCES IN FRACTURE RESEARCH, VOLS 1-6, 1997, : 431 - 437
12345