Study of oxidation and passivation behavior of Fe noparticles

被引：0
|
作者：
Wang, Min [1 ]
机构：
[1] Changchun Inst Technol, Changchun 130012, Jilin, Peoples R China
来源：
ADVANCED MATERIALS AND STRUCTURES, PTS 1 AND 2 | 2011年 / 335-336卷
关键词：
nanoparticles; oxidation; Passivate;
D O I：
10.4028/www.scientific.net/AMR.335-336.415
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fe nanoparticles prepared by the arc was used in the present study. It was oxidized by laying in the air and passivated by argon ion bombardment. The microsturcture, oxygen content and oxygen atom position in oxidized Fe nanoparticles were investigated. Furthermore, the variation of oxygen content with time in the passivated Fe nanoparticles and Fe nonparticles was also studied. The results showed that the effective size of oxidized Fe nanoparticles was about 10nm-40nm, and oxidation process was conducted on the surface. On the other hand, the oxygen content in passivated Fe nanoparticles reduced by comparing with that laying in the air for the same time.
引用
收藏
页码：415 / 418
页数：4
相关论文
共 50 条
  • [41] FORMATION KINETICS OF PASSIVATION FILM .1. THEORETIC STUDY OF INTENSIOSTATIC OXIDATION
    FOULETIER, M
    GUITTON, J
    BESSON, J
    ELECTROCHIMICA ACTA, 1976, 21 (11) : 1071 - 1077
  • [42] MECHANISM OF OXIDATION AND PASSIVATION OF IRON BY WATER-VAPOR - ELECTRON SPECTROSCOPIC STUDY
    ROBERTS, MW
    WOOD, PR
    JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1977, 11 (04) : 431 - 437
  • [43] CORROSION AND PASSIVATION OF FE AND FEN FILMS
    BRUSIC, V
    FRANKEL, GS
    RUSH, BM
    SCHROTT, AG
    JAHNES, C
    RUSSAK, MA
    PETERSEN, T
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1992, 139 (06) : 1530 - 1535
  • [44] STUDY OF FE(II) OXIDATION IN GROUND MAGNETITE
    SANCHEZ, RMT
    CURT, EM
    VOLZONE, C
    MERCADER, RC
    CAVALIERI, AL
    MATERIALS RESEARCH BULLETIN, 1990, 25 (05) : 553 - 561
  • [45] Study on Oxidation Behavior of Beryllium Bronze
    Zhang, Yulong
    Zhang, Weifang
    Zhang, Aiai
    Zhao, Shijun
    ADVANCED ENGINEERING MATERIALS III, PTS 1-3, 2013, 750-752 : 683 - 686
  • [46] Study of oxidation behavior of Zn nanoparticles
    Wang, Min
    NEW MATERIALS, APPLICATIONS AND PROCESSES, PTS 1-3, 2012, 399-401 : 565 - 568
  • [47] A LEED-AES STUDY OF OXIDATION OF FE(100) AND FE(110)
    LEYGRAF, C
    EKELUND, S
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY, 1974, 11 (01): : 189 - 189
  • [48] LEED-AES STUDY OF OXIDATION OF FE (110) AND FE (100)
    LEYGRAF, C
    EKELUND, S
    SURFACE SCIENCE, 1973, 40 (03) : 609 - 635
  • [49] Heterogeneous reduction of transition metals on Fe(II) oxide and silicate surfaces and the role of passivation by surface oxidation.
    White, AF
    Peterson, ML
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1997, 213 : 130 - GEOC
  • [50] Understanding the Oxidation Behavior of Fe/Ni/Cr and Fe/Cr/Ni Core/Alloy Nanoparticles
    Pathade, Laxmikant
    Doane, Tennyson L.
    Slaton, Rahiem Davon
    Maye, Mathew M.
    JOURNAL OF PHYSICAL CHEMISTRY C, 2016, 120 (38): : 22035 - 22044
12345