Study of oxidation and passivation behavior of Fe noparticles

被引：0
|
作者：
Wang, Min [1 ]
机构：
[1] Changchun Inst Technol, Changchun 130012, Jilin, Peoples R China
来源：
ADVANCED MATERIALS AND STRUCTURES, PTS 1 AND 2 | 2011年 / 335-336卷
关键词：
nanoparticles; oxidation; Passivate;
D O I：
10.4028/www.scientific.net/AMR.335-336.415
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fe nanoparticles prepared by the arc was used in the present study. It was oxidized by laying in the air and passivated by argon ion bombardment. The microsturcture, oxygen content and oxygen atom position in oxidized Fe nanoparticles were investigated. Furthermore, the variation of oxygen content with time in the passivated Fe nanoparticles and Fe nonparticles was also studied. The results showed that the effective size of oxidized Fe nanoparticles was about 10nm-40nm, and oxidation process was conducted on the surface. On the other hand, the oxygen content in passivated Fe nanoparticles reduced by comparing with that laying in the air for the same time.
引用
收藏
页码：415 / 418
页数：4
相关论文
共 50 条
  • [21] A STUDY OF THE OXIDATION PROCESS ON AN FE SURFACE
    CHEN, YQ
    LIN, ZD
    WU, SY
    QI, SX
    WU, XL
    CHINESE PHYSICS, 1988, 8 (04): : 929 - 932
  • [22] Passivation of sulfide mineral oxidation used by coating agent: Field study
    Choi, Jaeyoung
    Yang, Jung-Seok
    Kwon, Man Jae
    Park, Young-Tae
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2012, 243
  • [23] STUDY OF THE PASSIVATION FILMS ON FE-CR ALLOYS BY MODULATION SPECTROSCOPY
    HARA, N
    SUGIMOTO, K
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1979, 126 (08) : 1328 - 1334
  • [24] Oxidation Behavior of Fe-Al, Fe-Si and Fe-Al-Si Intermetallics
    Novak, Pavel
    Nova, Katerina
    MATERIALS, 2019, 12 (11):
  • [25] Formation and oxidation behavior of Al-Cu-Fe quasicrystal
    Zhou, CG
    Xu, HB
    Gong, SK
    Kang, GM
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2002, 18 (03) : 251 - 253
  • [26] Characterization of oxidation behavior at Fe-Si alloy surface
    Yanagihara, Katsuyuki
    Yamazaki, Shuichi
    Nippon Steel Technical Report, 2011, (100): : 27 - 32
  • [27] Oxidation behavior of a Fe/MnO ultrathin film studied by XPS
    Di Castro, V
    Ciampi, S
    Sestili, L
    SURFACE REVIEW AND LETTERS, 1998, 5 (01) : 393 - 396
  • [28] Oxidation behavior of Fe-Ni alloy at high temperature
    Son, KS
    Yoon, JH
    Kim, HS
    Narita, T
    HIGH TEMPERATURE CORROSION AND MATERIALS CHEMISTRY IV, 2003, 2003 (16): : 128 - 134
  • [29] Oxidation behavior of Al-Cu-Fe nanoquasicrystal powders
    Srinivas, V
    Barua, P
    Ghosh, TB
    Murty, BS
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2004, 334 : 540 - 543
  • [30] Formation and Oxidation Behavior of Al-Cu-Fe Quasicrystal
    Chungen ZHOU
    JournalofMaterialsScience&Technology, 2002, (03) : 251 - 253
12345