Study of oxidation and passivation behavior of Fe noparticles

被引：0
|
作者：
Wang, Min [1 ]
机构：
[1] Changchun Inst Technol, Changchun 130012, Jilin, Peoples R China
来源：
ADVANCED MATERIALS AND STRUCTURES, PTS 1 AND 2 | 2011年 / 335-336卷
关键词：
nanoparticles; oxidation; Passivate;
D O I：
10.4028/www.scientific.net/AMR.335-336.415
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fe nanoparticles prepared by the arc was used in the present study. It was oxidized by laying in the air and passivated by argon ion bombardment. The microsturcture, oxygen content and oxygen atom position in oxidized Fe nanoparticles were investigated. Furthermore, the variation of oxygen content with time in the passivated Fe nanoparticles and Fe nonparticles was also studied. The results showed that the effective size of oxidized Fe nanoparticles was about 10nm-40nm, and oxidation process was conducted on the surface. On the other hand, the oxygen content in passivated Fe nanoparticles reduced by comparing with that laying in the air for the same time.
引用
收藏
页码：415 / 418
页数：4
相关论文
共 50 条
  • [1] Study Of Oxidation Behavior Of Zn And Fe Nanoparticles
    Wang, Min
    MANUFACTURING ENGINEERING AND AUTOMATION II, PTS 1-3, 2012, 591-593 : 1071 - 1074
  • [2] PASSIVATION AND PROMOTION OF OXIDATION - REACTION OF OXYGEN WITH FE/GAAS(100)
    LI, N
    MENG, G
    XIE, K
    LIN, ZD
    SURFACE SCIENCE, 1991, 259 (03) : 301 - 313
  • [3] APPLICATIONS OF TEM TO THE PASSIVATION AND OXIDATION STUDIES OF FE-CR ALLOYS
    TJONG, SC
    METALS FORUM, 1985, 8 (01): : 49 - 55
  • [4] Oxidation behavior of Ta thin films as a passivation layer deposited on Cu
    Ichikawa, Takaaki
    Takeyama, Mayumi
    Noya, Atsushi
    Japanese Journal of Applied Physics, Part 1: Regular Papers & Short Notes & Review Papers, 1996, 35 (03): : 1844 - 1845
  • [5] Oxidation behavior of Ta thin films as a passivation layer deposited on Cu
    Ichikawa, T
    Takeyama, M
    Noya, A
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1996, 35 (03): : 1844 - 1845
  • [6] Oxidation Behavior of Copper at a Temperature below 300 °C and the Methodology for Passivation
    Lee, Shao-Kuan
    Hsu, Hsiu-Ching
    Tuan, Wei-Hsing
    MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2016, 19 (01): : 51 - 56
  • [7] ELLIPSOMETRIC STUDY OF THE ELECTROCHEMICAL MECHANISM OF THE PASSIVATION OF FE-CR ALLOYS DURING GAS OXIDATION BY ALTERNATING-CURRENT
    KOTENEV, VA
    FOKIN, MN
    PROTECTION OF METALS, 1995, 31 (01): : 46 - 51
  • [8] Oxidation Behavior of ODS Fe–Cr Alloys
    B A. Pint
    I. G. Wright
    Oxidation of Metals, 2005, 63 : 193 - 213
  • [9] The oxidation behavior of Fe-Al alloys
    Pint, BA
    Wright, IG
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 6, PRT 1 AND 2, PROCEEDINGS, 2004, 461-464 : 799 - 806
  • [10] BEHAVIOR OF FE IMPURITY DURING HCL OXIDATION
    HONDA, K
    OHSAWA, A
    NAKANISHI, T
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1995, 142 (10) : 3486 - 3492
12345